Evoprene™ Super G 948
| Category: | SEBS , Styrene Ethylene Butylene Styrene Block Copolymer |
| Manufacturer: | AlphaGary |
| Trademark: | Evoprene™ Super G |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ct9hRl_Evoprene-Super-G-948.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Evoprene™ Super G compounds are high performance SEBS-based TPE materials. They are formulated with a special resin modifier which increases the size of the end blocks. They are also compounded in a special way to ensure maximum dispersion of the various ingredients. The larger end blocks increase the glass transition temperature (Tg) providing two major practical advantages over regular SEBS-based compounds: improved heat resistance and improved recovery properties. The improved heat resistance raises the service temperature over regular SEBS-based grades by 10-15 deg C (18-25 deg F) and improves injection moulding cycle times by allowing the parts to be demoulded at a higher temperature without distortion. The improved recovery properties, as measured by compression set, provide much better sealing characteristics as explained overleaf. These compounds do need higher processing temperatures for best results. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.08 | g/cm³ | ISO 2781 |
| Molding Shrinkage | 1.2 to 3.5 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore A) | 44 | ISO 868 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (100% Strain) | 1.40 | MPa | ISO 37 |
| Tensile Stress (Yield) | 7.40 | MPa | ISO 37 |
| Tensile Elongation (Break) | 510 | % | ISO 37 |
| Tear Strength 1 | 20 | kN/m | ISO 34-1 |
| Compression Set | ISO 815 | ||
| 22°C, 72 hr | 12 | % | |
| 70°C, 22 hr | 18 | % | |
| 100°C, 22 hr | 31 | % |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| M-S Flow | 1.47 | MPa | Internal Method |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Suggested Max Regrind | 20 | % | |
| Rear Temperature | 200 to 220 | °C | |
| Middle Temperature | 200 to 220 | °C | |
| Front Temperature | 200 to 220 | °C | |
| Nozzle Temperature | 200 to 220 | °C | |
| Processing (Melt) Temp | 280 | °C | |
| Mold Temperature | 40.0 to 60.0 | °C | |
| Injection Rate | Moderate | ||
| Vent Depth | 0.020 to 0.050 | mm |
| Note Message | |
|---|---|
| 1 . | Method Ba, Angle (Unnicked) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Quantum Composites QC-7752 | Quantum Composites Inc. | Polyester, TS | Quantum Composites |
| TOTAL Polypropylene PPH 6080 | TOTAL Refining & Chemicals | PP Homopolymer | TOTAL Polypropylene |
| Unichem 1114-05 | Colorite Polymers | PVC, Rigid | Unichem |
| Nypol® PA A3 BGE0072 NR319 | Petropol Industry and Trade of Polymers LTDA | Nylon 66 | Nypol® PA |
| Fluon® PTFE G201 | Asahi Glass Co., Ltd. | PTFE | Fluon® |