Clearflex® H&T CLH 108
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | Versalis S.p.A. |
| Trademark: | Clearflex® H&T |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ct8m85_Clearflex-H-T-CLH-108.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Clearflex H&T CLH 108 is an octene copolymer linear low density polyethylene (C8-LLDPE), with antioxidants, suitable for cast film extrusion. Stretch films obtained from Clearflex H&T CLH 108 show excellent optical properties, high fracture mechanical characteristics, together with excellent performances in automatic wrapping machines (holding force, prestretch). Main Application Clearflex H&T CLH 108 is suggested for production of very-high pre-stretch film. The combination of high mechanical properties and low gel content can allow "downgauging" for many applications. In addition to that, for its high resistance to tear propagation and to puncture, together with an outstanding holding force, Clearflex H&T CLH 108 is recommended for "critical" packaging (i.e irregular shape loads, presence of sharp edges, etc…) or loads subjected to severe mechanical stresses during transportation. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.919 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 2.5 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction (vs. Itself - Dynamic, Cast Film) | > 0.50 | ISO 8295 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 23 | µm | |
| Film Thickness - Recommended / Available | 8 to 50µm | ||
| Tensile Modulus | ISO 527-3 | ||
| 1% Secant, MD : 23 µm, Cast Film | 140 | MPa | |
| 1% Secant, TD : 23 µm, Cast Film | 150 | MPa | |
| Tensile Stress | ISO 527-3 | ||
| MD : Yield, 23 µm, Cast Film | 9.00 | MPa | |
| TD : Yield, 23 µm, Cast Film | 10.0 | MPa | |
| MD : Break, 23 µm, Cast Film | 48.0 | MPa | |
| TD : Break, 23 µm, Cast Film | 40.0 | MPa | |
| Tensile Elongation | ISO 527-3 | ||
| MD : Break, 23 µm, Cast Film | 600 | % | |
| TD : Break, 23 µm, Cast Film | 800 | % | |
| Dart Drop Impact 1(23 µm, Cast Film) | 170 | g | ISO 7765-1 |
| Elmendorf Tear Strength 2 | ISO 6383-2 | ||
| MD : 23.0 µm | 130.0 | kN/m | |
| TD : 23.0 µm | 170.0 | kN/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -70.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 95.0 | °C | ISO 306/A |
| Melting Temperature | 120 | °C | Internal Method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 23.0 µm, Cast Film) | 93 | ASTM D2457 | |
| Haze (23.0 µm, Cast Film) | 0.80 | % | ISO 14782 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 220 to 270 | °C |
| Note Message | |
|---|---|
| 1 . | F50 |
| 2 . | Cast Film |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SUPREME Specialty PS SP6520 | Supreme Petrochem Ltd. | PS (Specialty) | SUPREME Specialty PS |
| DOW™ HDPE NG6997 | The Dow Chemical Company | HDPE | DOW™ HDPE |
| Fainplast PVC GK 88/3 | Fainplast Compounds S.r.l | PVC, Unspecified | Fainplast PVC |
| OmniTech™ ABS 63 | OMNI Plastics, LLC | ABS | OmniTech™ |
| EPAMOULD 660D12 | Epaflex Polyurethanes S.R.L. | TPU-Polyester | EPAMOULD |