Generic Nylon 6 - Mineral
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ct5GgU_Generic-Nylon-6---Mineral.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic Nylon 6 - Mineral This information is provided for comparative purposes only. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.32 - 1.49 | g/cm³ | ASTM D792 |
| 23°C | 1.21 - 1.50 | g/cm³ | ISO 1183 |
| Apparent Density | 0.70 | g/cm³ | ISO 60 |
| Melt Mass-Flow Rate (MFR) (235°C/2.16 kg) | 3.0 - 33 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) (275°C/5.0 kg) | 28.0 - 90.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | |||
| Flow : 23°C | 0.28 - 1.2 | % | ASTM D955 |
| Transverse flow : 23°C | 0.39 - 1.0 | % | ASTM D955 |
| 23°C | 0.28 - 1.1 | % | ISO 294-4 |
| Water Absorption | |||
| 23°C, 24 hr | 0.060 - 1.3 | % | ASTM D570 |
| 23°C, 24 hr | 0.89 - 1.2 | % | ISO 62 |
| Saturated, 23°C | 1.5 - 6.6 | % | ASTM D570 |
| Saturated, 23°C | 5.4 - 8.0 | % | ISO 62 |
| Equilibrium, 23°C | 0.85 - 2.1 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.040 - 2.4 | % | ISO 62 |
| Viscosity Number | 145 | cm³/g | ISO 307 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | |||
| 23°C | 75 - 122 | ASTM D785 | |
| 23°C | 115 - 119 | ISO 2039-2 | |
| Ball Indentation Hardness | 169 - 215 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| 23°C | 3500 - 13800 | MPa | ASTM D638 |
| 23°C | 3300 - 9000 | MPa | ISO 527-2 |
| Tensile Strength | |||
| Yield, 23°C | 68.6 - 131 | MPa | ASTM D638 |
| Yield, 23°C | 63.8 - 92.5 | MPa | ISO 527-2 |
| Fracture, 23°C | 51.0 - 91.0 | MPa | ASTM D638 |
| Fracture, 23°C | 64.2 - 121 | MPa | ISO 527-2 |
| 23°C | 57.4 - 113 | MPa | ASTM D638 |
| Tensile Elongation | |||
| Yield, 23°C | 2.0 - 4.3 | % | ASTM D638 |
| Yield, 23°C | 2.9 - 3.5 | % | ISO 527-2 |
| Fracture, 23°C | 0.70 - 13 | % | ASTM D638 |
| Fracture, 23°C | 2.5 - 6.1 | % | ISO 527-2 |
| Flexural Modulus | |||
| 23°C | 3420 - 7490 | MPa | ASTM D790 |
| 23°C | 2750 - 7880 | MPa | ISO 178 |
| Flexural Strength | |||
| 23°C | 95.9 - 193 | MPa | ASTM D790 |
| 23°C | 88.8 - 174 | MPa | ISO 178 |
| Yield, 23°C | 70.0 - 196 | MPa | ASTM D790 |
| Fracture, 23°C | 75.0 - 130 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23°C | 43.9 - 49.0 | J/m | ASTM D256 |
| 23°C | 1.8 - 10 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 30 - 51 | kJ/m² | ISO 179 |
| Notched Izod Impact | |||
| 23°C | 26 - 66 | J/m | ASTM D256 |
| 23°C | 3.0 - 11 | kJ/m² | ISO 180 |
| Unnotched Izod Impact | |||
| 23°C | 44 - 470 | J/m | ASTM D256 |
| 23°C | 18 - 100 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, not annealed | 189 - 210 | °C | ASTM D648 |
| 0.45 MPa, not annealed | 178 - 217 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 103 - 208 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 66.6 - 206 | °C | ISO 75-2/A |
| Continuous Use Temperature | 67.6 - 162 | °C | ASTM D794 |
| Vicat Softening Temperature | |||
| -- | 190 - 210 | °C | ASTM D1525 |
| -- | 199 - 200 | °C | ISO 306 |
| Melting Temperature | |||
| -- | 213 - 222 | °C | |
| -- | 220 | °C | DSC |
| -- | 220 - 222 | °C | ISO 11357-3 |
| -- | 218 - 220 | °C | ASTM D3418 |
| -- | 218 - 223 | °C | ISO 3146 |
| Linear thermal expansion coefficient | |||
| Flow | 2.9E-5 - 5.7E-5 | cm/cm/°C | ASTM D696 |
| Flow | 1.6E-5 - 5.0E-5 | cm/cm/°C | ASTM E831 |
| Flow | 3.4E-5 - 6.6E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral | 2.8E-5 - 8.7E-5 | cm/cm/°C | ASTM E831 |
| Lateral | 4.9E-5 - 7.1E-5 | cm/cm/°C | ISO 11359-2 |
| Thermal Conductivity | |||
| 23°C | 1.3 - 10 | W/m/K | ASTM C177 |
| 23°C | 0.27 - 8.6 | W/m/K | ISO 8302 |
| RTI Elec | 65.0 - 121 | °C | UL 746 |
| RTI Imp | 65.0 - 120 | °C | UL 746 |
| RTI | 65.0 - 121 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | |||
| -- | 5.1E+4 - 2.5E+15 | ohms | ASTM D257 |
| -- | 1.0E+10 - 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | |||
| 23°C | 1.0E+11 - 2.5E+15 | ohms·cm | ASTM D257 |
| 23°C | 1.0E+12 - 2.5E+15 | ohms·cm | IEC 60093 |
| Dielectric Strength | |||
| 23°C | 13 - 25 | kV/mm | ASTM D149 |
| 23°C | 15 - 35 | kV/mm | IEC 60243-1 |
| Dielectric Constant | |||
| 23°C | 3.43 - 7.27 | ASTM D150 | |
| 23°C | 3.50 - 5.00 | IEC 60250 | |
| 23°C | 3.64 | IEC 60250 | |
| Dissipation Factor | |||
| 23°C | 0.042 - 0.083 | ASTM D150 | |
| 23°C | 5.0E-3 - 0.021 | IEC 60250 | |
| Arc Resistance | 128 - 190 | sec | ASTM D495 |
| Comparative Tracking Index | 438 - 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate | 0.0 - 100 | mm/min | ISO 3795 |
| Glow Wire Flammability Index | 650 - 960 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature | 650 - 751 | °C | IEC 60695-2-13 |
| Oxygen Index | 24 - 32 | % | ISO 4589-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 79.3 - 90.3 | °C | |
| Drying Time | 2.9 - 5.3 | hr | |
| Suggested Max Moisture | 0.10 - 0.20 | % | |
| Suggested Max Regrind | 18 | % | |
| Hopper Temperature | 70.0 - 240 | °C | |
| Rear Temperature | 225 - 275 | °C | |
| Middle Temperature | 239 - 289 | °C | |
| Front Temperature | 239 - 286 | °C | |
| Nozzle Temperature | 238 - 286 | °C | |
| Processing (Melt) Temp | 249 - 293 | °C | |
| Mold Temperature | 59.6 - 101 | °C | |
| Injection Pressure | 6.89 - 95.2 | MPa | |
| Holding Pressure | 41.4 - 75.0 | MPa | |
| Back Pressure | 0.172 - 6.03 | MPa | |
| Screw Speed | 40 - 91 | rpm |
| Injection instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic Nylon 6 - MineralThis information is provided for comparative purposes only. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TEKNIFLEX® VPA10200 | Tekni-Films, a div of Tekni-Plex | Film, PVC/PE/PCTFE | TEKNIFLEX® |
| TEKNIFLEX® VPA7400 | Tekni-Films, a div of Tekni-Plex | Film, PVC/PE/PCTFE | TEKNIFLEX® |
| Buna® EP G 6850 | LANXESS Corporation | EPDM | Buna® EP |
| Cogegum® GFR/380 | Solvay Specialty Polymers | Polyolefin, Unspecified | Cogegum® |
| Gallonprene® GP200-20 | Shenzhen Sungallon Rubber & Plastic Corporation Limited | TPE | Gallonprene® |