Lucet® GB-325
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | LG Chem Ltd. |
| Trademark: | Lucet® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | crolWt_Lucet-GB-325.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Lucet® GB-325 is an Acetal (POM) Copolymer material filled with 25% glass bead. It is available in North America for injection molding. Important attributes of Lucet® GB-325 are:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.59 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 1.3 to 1.7 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.20 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 85 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 63.7 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 10 | % | ASTM D638 |
| Flexural Modulus | 3920 | MPa | ASTM D790 |
| Flexural Strength (Yield) | 98.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -40°C | 29 | J/m | |
| 23°C | 39 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 163 | °C | |
| 1.8 MPa, Unannealed | 150 | °C | |
| CLTE - Flow | 9.0E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+16 | ohms | ASTM D257 |
| Volume Resistivity | 1.0E+14 | ohms·cm | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.794 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 100 | °C | |
| Drying Time | 3.0 to 6.0 | hr | |
| Rear Temperature | 170 to 190 | °C | |
| Middle Temperature | 190 to 210 | °C | |
| Front Temperature | 200 to 225 | °C | |
| Nozzle Temperature | 200 to 225 | °C | |
| Processing (Melt) Temp | 210 to 220 | °C | |
| Mold Temperature | 60.0 to 80.0 | °C | |
| Injection Pressure | 68.6 to 118 | MPa | |
| Back Pressure | 0.00 to 3.92 | MPa | |
| Screw Speed | 40 to 75 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 687 FR HEC | RTP Company | ABS | RTP |
| RIALFILL B 15 SA 28 TC | RIALTI Srl | PP, Unspecified | RIALFILL |
| Shandong PA/PP PA6/PP | Shandong Dongchen Engineering Plastics Co., Ltd. | Nylon 6+PP | Shandong PA/PP |
| Hostaform® S 9364LPB | Celanese Corporation | Acetal (POM) Copolymer | Hostaform® |
| KOPA® KN133G30BL | Kolon Plastics, Inc. | Nylon 6 | KOPA® |