| Category: | PMP Copolymer , Polymethylpentene Copolymer |
| Manufacturer: | Mitsui Chemicals America, Inc. |
| Trademark: | TPX™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | cr7Rz0_TPXDX560M.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| TPX™DX560M is a polymethylpentene copolymer (PMP copolymer) material,. This product is available in North America. The processing methods are: blow molding, pipeline extrusion molding, extrusion, profile extrusion molding or injection molding. |
| General Information | |
|---|---|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.856 | g/cm³ | Internal method |
| Melt Mass-Flow Rate (MFR) (260°C/5.0 kg) | 33 | g/10 min | Internal method |
| Water Absorption (Saturation) | < 0.010 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | < 50 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1(23°C, Injection Molded) | 280 | MPa | ASTM D638 |
| Tensile Strength 2 | ASTM D638 | ||
| Yield, 23°C, injection molding | 8.00 | MPa | ASTM D638 |
| Fracture, 23°C, injection molding | 9.00 | MPa | ASTM D638 |
| Tensile Elongation 3(Break, 23°C, Injection Molded) | 100 | % | ASTM D638 |
| Flexural Modulus 4(mm, injection molding, 51.0mm span) | 190 | MPa | ASTM D790 |
| Flexural Strength 5(mm, injection molding, 51.0mm span) | 6.00 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (Injection Molded) | 500 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C, Injection Molded) | No Break | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load 6(0.45 MPa, Unannealed, 6.35 mm) | 59.0 | °C | ASTM D648 |
| Vicat Softening Temperature | 89.0 | °C | ASTM D1525 7 |
| Peak Crystallization Temperature (DSC) | 221 | °C | ASTM D3418 |
| CLTE - Flow (-10 to 160°C) | 3.5E-4 | cm/cm/°C | Internal method |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity 8(2.00 mm) | > 1.0E+15 | ohms·cm | ASTM D257 |
| Dielectric Strength 9(2.00 mm) | 31 | kV/mm | ASTM D149 |
| Dielectric Constant 10(2.00 mm, 1 MHz) | 2.15 | ASTM D150 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 270 | °C | |
| Middle Temperature | 280 | °C | |
| Front Temperature | 300 | °C | |
| Mold Temperature | 20 - 60 | °C | |
| Injection Pressure | 30.0 - 40.0 | MPa | |
| Holding Pressure | 30.0 | MPa |
| Injection instructions |
|---|
| Zone 4 Temperature: 300°C |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 280 | °C | |
| Cylinder Zone 2 Temp. | 290 | °C | |
| Cylinder Zone 3 Temp. | 290 | °C | |
| Cylinder Zone 4 Temp. | 290 | °C | |
| Adapter Temperature | 290 | °C | |
| Die Temperature | 290 | °C |
| Note Message | |
|---|---|
| 1 . | Type 4, 50mm/min |
| 2 . | Type 4, 50mm/min |
| 3 . | Type 4, 50mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 1.3 mm/min |
| 6 . | 120°C/hr |
| 7 . | 速率 A (50°C/h), 压 力1 (10N) |
| 8 . | Injection Molded |
| 9 . | Injection Molded |
| 10 . | Injection Molded |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Borealis PP EE002AE | Borealis AG | PP, Unspecified | Borealis PP |
| CERTENE鈩?HI-954 | Muehlstein | HDPE | CERTENE™ |
| LTP ZW-3625 | Chengdu Letian Plastics Co., Ltd | PPS Alloy | LTP |
| LUVOCOM® 1100-7337/WT | Lehmann & Voss & Co. | PESU | LUVOCOM® |
| 3M™ Dyneon™ Fluoroelastomer FPO 3520 | 3M Advanced Materials Division | Fluorelastomer | 3M™ Dyneon™ Fluoroelastomer |