Menzolit® CIC 1400
| Category: | Polyester, TS , Thermoset Polyester |
| Manufacturer: | Menzolit Ltd (UK) |
| Trademark: | Menzolit® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | cqv44O_Menzolit-CIC-1400.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Menzolit® CIC 1400 is a DMC/BMC (CIC = continues impregnated compound) like material. High strength material resistant to fuel, lubricants and cleaning agents being used around automotive engines. Examples are valve covers, carburettor housings. UL approv |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Part Marking Code (ISO 11469) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.63 | g/cm³ | ISO 1183 |
| Molding Shrinkage | 0.030 | % | ISO 294-4 |
| Water Absorption (Saturation, 23°C) | 0.50 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (Compression Molded) | 7000 | MPa | ISO 527-2 |
| Tensile Stress (Yield, Compression Molded) | 40.0 | MPa | ISO 527-2 |
| Flexural Modulus (Compression Molded) | 7000 | MPa | ISO 178 |
| Flexural Stress (Compression Molded) | 100 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (Compression Molded) | 40 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glass Transition Temperature | 162 | °C | DSC |
| CLTE - Flow | 1.0E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+14 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+12 | ohms·cm | IEC 60093 |
| Comparative Tracking Index | 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (3.00 mm) | HB | UL 94 | |
| Glow Wire Ignition Temperature | 750 | °C | IEC 60695-2-13 |
| Oxygen Index | 22 | % | ISO 4589-2 |
| Additional Information |
|---|
| Shrinkage, ISO 2577: 0.03%Post Moulding Shrinkage, DIN 53464: 0%Heat Distortion Temperature, EN ISO 75-2: >150°CContinuous Service Temperature, Menzolit Method: 170°CGlow Bar, IEC 60707-3: BH2 <= 95 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Mold Temperature | 150 - 170 | °C | |
| Injection Pressure | 8.00 - 10.0 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Wellamid® FRGS25-66-NBK3 | Wellman Engineering Resins | Nylon 66 | Wellamid® |
| Ultron® 150C6-WR | Asia International Enterprise (Hong Kong) Limited | PEI | Ultron® |
| Halene P M315 | Haldia Petrochemicals Ltd. | PP Impact Copolymer | Halene P |
| Hifax EYG 382P C12716 | LyondellBasell Industries | PP Copolymer | Hifax |
| ICORENE® N1007 | ICO Polymers EMEA, A Division of A. Schulman | EVA | ICORENE® |