Monprene® OM-16260
| Category: | TPE , Thermoplastic Elastomer |
| Manufacturer: | Teknor Apex Company |
| Trademark: | Monprene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | cq0Sli_Monprene-OM-16260.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Monprene®OM-16260 is a thermoplastic elastomer (TPE) material,. This product is available in the Asia-Pacific region and is processed by extrusion or injection molding. Monprene®The main characteristics of the OM-16260 are: flame retardant/rated flame. Typical application areas include:
|
| General Information | |
|---|---|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.996 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (200°C/5.0 kg) | 10 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A) | 60 | ASTM D2240 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (300% Strain) | 4.14 | MPa | ASTM D412 |
| Tensile Strength (Break) | 8.27 | MPa | ASTM D412 |
| Tensile Elongation (Break) | 560 | % | ASTM D412 |
| Compression Set (23°C, 22 hr) | 28 | % | ASTM D395 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| RTI Elec | 50.0 | °C | UL 746 |
| RTI Imp | 50.0 | °C | UL 746 |
| RTI | 50.0 | °C | UL 746 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.00 to 1.20mm, All Colors) | HB | UL 94 |
| Additional Information | Nominal Value | ||
|---|---|---|---|
| Adhesion to ABS | |||
| Adhesion to PC | |||
| Adhesion to PC/ABS |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 60.0 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Rear Temperature | 138 - 160 | °C | |
| Middle Temperature | 182 - 199 | °C | |
| Front Temperature | 182 - 199 | °C | |
| Nozzle Temperature | 193 - 210 | °C | |
| Processing (Melt) Temp | 177 - 199 | °C | |
| Mold Temperature | 4.44 - 48.9 | °C | |
| Injection Pressure | 1.38 - 5.52 | MPa | |
| Back Pressure | 0.172 - 0.862 | MPa | |
| Screw Speed | 50 - 100 | rpm | |
| Cushion | 3.81 - 25.4 | mm |
| Injection instructions |
|---|
| Moisture can degrade the material. Drying is suggested. This can be accomplished by placing the material in a desiccant dryer for 2 to 4 hours at 140°F. |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 138 - 149 | °C | |
| Cylinder Zone 2 Temp. | 149 - 160 | °C | |
| Cylinder Zone 3 Temp. | 160 - 182 | °C | |
| Cylinder Zone 5 Temp. | 171 - 193 | °C | |
| Die Temperature | 182 - 204 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Marlex® PP HGZ-120SP | Saudi Polymers Company | PP Homopolymer | Marlex® PP |
| 3M™ Dyneon™ PTFE Compound TF 6221 | 3M Advanced Materials Division | PTFE | 3M™ Dyneon™ PTFE Compound |
| Karina RED PVC COMPOUND -E 780-42/179-A-IS (C800) | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Optix® CA-80 | Plaskolite West, Inc. | Acrylic (PMMA) | Optix® |
| Sylvin 6177-80 Orange 5102 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |