EvoSource™ PC/ABS 5366 90/04
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | MBA Polymers Austria Kunststoffverarbeitung GmbH |
| Trademark: | EvoSource™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | cpeXZo_EvoSourcePCABS53669004.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
This is a recycled PCABS from post-consumer sources and modified for technical applications demanding improved properties:
|
| General Information | |
|---|---|
| Recycled Content |
|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.17 | g/cm³ | Internal method |
| Melt Mass-Flow Rate (MFR) (240°C/5.0 kg) | 20 | g/10 min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| -- | 0.53 | % | ISO 294-4 |
| 48 hours | 0.58 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 2300 | MPa | ISO 527-2/1 |
| Tensile Stress (23°C) | 50.0 | MPa | ISO 527-2/50 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/A | ||
| -30°C | 10 | kJ/m² | ISO 179/A |
| 23°C | 25 | kJ/m² | ISO 179/A |
| Charpy Unnotched Impact Strength | ISO 179 | ||
| -30°C | 90 | kJ/m² | ISO 179 |
| 23°C | 140 | kJ/m² | ISO 179 |
| Notched Izod Impact (23°C) | 25 | kJ/m² | ISO 180/A |
| Unnotched Izod Impact Strength (23°C) | 100 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 115 | °C | ISO 306/A50 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.5 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Processing (Melt) Temp | 235 - 260 | °C | |
| Mold Temperature | 70 - 90 | °C |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Melt Temperature | 250 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYSTONE® Marine-Tec lite | Röchling Engineering Plastics SE & Co. KG | TP, Unspecified | POLYSTONE® |
| TECHNYL® 2710IR BRIGHT | Solvay Engineering Plastics | Nylon 66 | TECHNYL® |
| Taizhou Phenolic PF2C3-431J | Taizhou Changxiong Plastic Co., Ltd. | Phenolic | Taizhou Phenolic |
| AvaSpire® AV-848 GF30 | Solvay Specialty Polymers | PAEK | AvaSpire® |
| Sylvin 4200-85 Brown 7424 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |