Braskem PE HF3712
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | Braskem |
| Trademark: | Braskem PE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | cpNg7D_Braskem-PE-HF3712.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
The HF3712 resin is a Linear Low Density Polyethylene (1) , produced through slurry loop process and indicated for the production of geomembranes. It shows excellent resistance to environmental stress cracking (ESCR), good processability and melt strength. Additive: Lubricant - Antioxidant. Application: Geomembranes. Recommended Processing Conditions: The HF3712 resin should be processed on specific extruders. The optimum processing conditions will vary according to the type of equipment used, but the best results are obtained at a melt temperature within the range of 175 to 195°C. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.937 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/21.6 kg) | 11 | g/10 min | ASTM D1238 |
| Environmental Stress-Cracking Resistance | |||
| -- 1 | > 900 | hr | ASTM D5397 |
| 2.00mm, 10% Igepal, molded, F50 | > 1500 | hr | ASTM D1693 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, Compression Molded) | 56 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield, 2.00mm, molded | 19.0 | MPa | ASTM D638 |
| Fracture, 2.00mm, molded | 28.0 | MPa | ASTM D638 |
| Tensile Elongation | ASTM D638 | ||
| Yield, 2.00mm, molded | 12 | % | ASTM D638 |
| Fracture, 2.00mm, molded | 1300 | % | ASTM D638 |
| Flexural Modulus - 1% Secant (2.00 mm, Compression Molded) | 682 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, Compression Molded) | 740 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed, Compression Molded) | 54.0 | °C | ASTM D648 |
| Vicat Softening Temperature | 62.0 | °C | ASTM D1525 2 |
| Extrusion instructions |
|---|
| The HF3712 resin should be processed on specific extruders. The optimum processing conditions will vary according to the type of equipment used, but the best results are obtained at a melt temperature within the range of 175 to 195°C. |
| Note Message | |
|---|---|
| 1 . | SP-NCTL |
| 2 . | 载荷2 (50N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ASACLEAN™ CP | ASACLEAN - Sun Plastech Inc. | Proprietary | ASACLEAN™ |
| Formolene® LH5206 | Formosa Plastics Corporation, U.S.A. | HDPE | Formolene® |
| HiFill® PA6 GF/M40 HS L BK | Techmer Engineered Solutions | Nylon 6 | HiFill® |
| Karina CLEAR PVC COMPOUND 833-IS-SD | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Lumiplas® LD7701FD | LG Chem Ltd. | PC | Lumiplas® |