| 4LOY 10E27300 is a Standard Flow 85% PC / 15% ABS PC/ABS |
| General Information | |
|---|---|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.15 | g/cm³ | ISO 1183 |
| Water Absorption 1(Equilibrium, 23°C, 50% RH) | 0.20 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 2300 | MPa | ISO 527-2/5 |
| Tensile Stress (Break, 23°C) | 45.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Break, 23°C) | 50 | % | ISO 527-2/5 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ISO 180/1A | ||
| -30°C | 42 | kJ/m² | ISO 180/1A |
| 23°C | 46 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 125 | °C | ISO 75-2/B |
| Vicat Softening Temperature | 128 | °C | ISO 306/B |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 | |
| Glow Wire Flammability Index (2.00 mm) | 650 | °C | IEC 60695-2-12 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 110 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Processing (Melt) Temp | 230 - 260 | °C | |
| Mold Temperature | 60.0 - 90.0 | °C | |
| Injection Rate | Moderate-Fast | ||
| Holding Pressure | 50.0 - 100 | MPa | |
| Screw Speed | 200 | rpm |
| Injection instructions |
|---|
| Feed Throat Temperature: 60 - 80 °CBack Pressure: Low |
| Note Message | |
|---|---|
| 1 . | 24 Hrs |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RMA 57 | Ronald Mark Associates, Inc. | PVC Homopolymer | RMA |
| Silamid® E | Roonamid a.s. | Nylon 6 | Silamid® |
| Cabofor® 28 V0 BIANCO 0199 | SO.F.TER. SPA | PC | Cabofor® |
| ELASTOSIL® LR 3003/03 A/B | Wacker Chemie AG | Silicone | ELASTOSIL® LR |
| LNP™ LUBRICOMP™ EL002 compound | SABIC Innovative Plastics | PEI | LNP™ LUBRICOMP™ |