LNP™ THERMOCOMP™ JF004P compound
| Category: | PESU , Polyethersulfone |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | coSc6C_LNPTHERMOCOMPJF004Pcompound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP JF004P is a compound based on Polyethersulfone resin containing Glass Fiber. Added features of this material include: Exceptional Processing. Also known as: LNP* THERMOCOMP* Compound JF-1004 EP Product reorder name: JF004P |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Molding Shrinkage - Flow (24 hr) | 0.30 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 7610 | MPa | ASTM D638 |
| Tensile Strength (Break) | 120 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 2.2 | % | ASTM D638 |
| Flexural Modulus | 7410 | MPa | ASTM D790 |
| Flexural Strength | 172 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 53 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 500 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.20 mm) | 207 | °C | ASTM D648 |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| QR Resin QR-2005IM | QTR, Inc. | ABS | QR Resin |
| 3M™ Dyneon™ PTFE Compound TFX 4262 | 3M Advanced Materials Division | PTFE | 3M™ Dyneon™ PTFE Compound |
| ARC ARC1420 | ARC Resin Corporation | ABS | ARC |
| Kingfa JH-R2G10 P60 | Kingfa | PC+ABS | Kingfa |
| Sylvin 9655-75 Clear 8384 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |