GAPEX® RPP10EB49WH
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Ferro Corporation |
| Trademark: | GAPEX® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | coNXto_GAPEX-RPP10EB49WH.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
GAPEX®RPP10EB49WH is a polypropylene homopolymer (PP Homopoly) material, and its filler is 10% glass fiber reinforced material. This product is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific,. GAPEX®The main features of the RPP10EB49WH are:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.988 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 13 | g/10 min | ASTM D1238 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 0.90 | % | ASTM D955 |
| Transverse flow | 1.3 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield, 23°C) | 44.8 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | 4.5 | % | ASTM D638 |
| Flexural Modulus | ASTM D790 | ||
| 1% secant : 23°C | 2570 | MPa | ASTM D790 |
| Tangent : 23°C | 2650 | MPa | ASTM D790 |
| Flexural Strength (Yield, 23°C) | 73.1 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 32 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 290 | J/m | ASTM D256 |
| Dart Drop Impact | 0.282 | J | ASTM D5420 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 146 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 110 | °C | ASTM D648 |
| Additional Information |
|---|
| Filler Content, ASTM D2584: 12% |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 71.1 - 82.2 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Rear Temperature | 221 - 238 | °C | |
| Middle Temperature | 227 - 243 | °C | |
| Front Temperature | 232 - 260 | °C | |
| Nozzle Temperature | 232 - 260 | °C | |
| Processing (Melt) Temp | 221 - 238 | °C | |
| Mold Temperature | 37.8 - 65.6 | °C | |
| Injection Rate | Slow-Moderate | ||
| Back Pressure | 0.138 - 0.345 | MPa | |
| Cushion | 5.08 - 12.7 | mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Prime Polypro™ J232WA | Prime Polymer Co., Ltd. | PP Random Copolymer | Prime Polypro™ |
| SCHULAMID® 6 MKF 3010 HI | A. Schulman Europe | Nylon 6 | SCHULAMID® |
| GPPS Microgranulates 170M | INEOS Styrenics International SA | PS (GPPS) | GPPS Microgranulates |
| Karina WHITE PVC COMPOUND 752D10/152-B-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LNP™ THERMOTUF™ VC006 compound | SABIC Innovative Plastics | Nylon 66 | LNP™ THERMOTUF™ |