Taitalac® 6000H
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Taita Chemical Company, Ltd. |
| Trademark: | Taitalac® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | cni61R_Taitalac-6000H.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Taitalac® 6000H is an Acrylonitrile Butadiene Styrene (ABS) material. It is available in Asia Pacific or North America for extrusion. Important attributes of Taitalac® 6000H are:
Typical applications include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.04 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 200°C/5.0 kg | 0.50 | g/10 min | |
| 220°C/10.0 kg | 5.5 | g/10 min | |
| Molding Shrinkage - Flow | < 0.40 | % | ASTM D955 |
| Water Absorption (24 hr) | < 0.30 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale, 23°C) | 115 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | ASTM D638 | ||
| Yield, 23°C, 3.18 mm | 46.9 | MPa | |
| Break, 23°C, 3.18 mm | 37.2 | MPa | |
| Tensile Elongation 2(Break, 23°C, 3.18 mm) | 30 | % | ASTM D638 |
| Flexural Modulus 3(23°C) | 2480 | MPa | ASTM D790 |
| Flexural Strength 4(Yield, 23°C) | 71.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| 23°C, 3.18 mm | 340 | J/m | |
| 23°C, 6.35 mm | 310 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 12.7 mm) | 88.9 | °C | ASTM D648 |
| Vicat Softening Temperature | 105 | °C | ASTM D1525 5 |
| RTI Elec (1.57 mm) | 60.0 | °C | UL 746 |
| RTI Imp (1.57 mm) | 60.0 | °C | UL 746 |
| RTI Str (1.57 mm) | 60.0 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| High Amp Arc Ignition (HAI) (1.57 mm) | 200 | UL 746 | |
| High Voltage Arc Tracking Rate (HVTR) (1.57 mm) | 0.00 | mm/min | UL 746 |
| Hot-wire Ignition (HWI) (1.57 mm) | 18 | sec | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.59 mm) | HB | UL 94 |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 5.0 mm/min |
| 3 . | 2.8 mm/min |
| 4 . | 2.8 mm/min |
| 5 . | Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Niretan B SV30 | Soredi S.p.a. | Nylon 6 | Niretan B |
| AlphaSeal™ 240-6CY BLUE 7002 | AlphaGary | TPE | AlphaSeal™ |
| Andur AL 70 DP/Curene® 442 | Anderson Development Company | PUR-Eth,aliphat | Andur |
| Delrin® 500TE NC010 | DuPont Performance Polymers | Acetal (POM) Homopolymer | Delrin® |
| POLYFORT® FPP 1005 | A. Schulman Inc. | PP, Unspecified | POLYFORT® |