Kepital® F30-52
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | Korea Engineering Plastics Co., Ltd |
| Trademark: | Kepital® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | cnV57K_Kepital-F30-52.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| A low viscosity U.V. stabilized grade suitable for outdoor use. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.41 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) | |||
| 190°C/2.16 kg | 26 | g/10 min | ASTM D1238 |
| -- | 28 | g/10 min | ISO 1133 |
| Molding Shrinkage | |||
| Flow : 3.00 mm | 2.0 | % | ASTM D955 |
| 3.00 mm | 2.0 | % | |
| Water Absorption (Equilibrium, 23°C, 60% RH) | 0.22 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| Yield, 23°C | 59.0 | MPa | ASTM D638 |
| Yield, 23°C | 63.0 | MPa | ISO 527-2 |
| Tensile Elongation (Break, 23°C) | 85 | % | ASTM D638 |
| Nominal Tensile Strain at Break | 37 | % | ISO 527-2 |
| Flexural Modulus | |||
| 23°C | 2580 | MPa | ASTM D790 |
| 23°C | 2450 | MPa | ISO 178 |
| Flexural Strength | |||
| 23°C | 85.0 | MPa | ASTM D790 |
| 23°C | 83.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 6.0 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact (3.20 mm) | 69 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 110 | °C | ASTM D648 |
| Peak Melting Temperature | 165 | °C | ASTM D3418 |
| CLTE - Flow (20 to 80°C) | 1.3E-4 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | |||
| -- | 1.0E+16 | ohms | ASTM D257 |
| -- | 1.0E+14 | ohms | IEC 60093 |
| Volume Resistivity | |||
| -- | 1.0E+14 | ohms·cm | ASTM D257 |
| -- | 1.0E+13 | ohms·cm | IEC 60093 |
| Dielectric Strength | 19 | kV/mm | ASTM D149, IEC 60243-1 |
| Dielectric Constant (1 MHz) | 3.70 | ASTM D150 | |
| Dissipation Factor (1 MHz) | 7.0E-3 | ASTM D150 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.800 mm) | HB | UL 94 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SCHULAMID® 6 GF 15 HI K2073 SCHWARZ 96.8001 | A. Schulman Europe | Nylon 6 | SCHULAMID® |
| ALTECH® PA6 A 2030/109 GF30 BK1128-12LS | ALBIS PLASTIC GmbH | Nylon 6 | ALTECH® PA6 |
| Gallonprene® GP410-7501 | Shenzhen Sungallon Rubber & Plastic Corporation Limited | TPE | Gallonprene® |
| Luranyl® HT 240 G4 | ROMIRA GmbH | PPE+Nylon 66 | Luranyl® |
| Rotuba CAB B9025 (8% Plasticizer) | Rotuba Extruders, Inc. | CAB | Rotuba CAB |