SABIC® LDPE PCG01
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | Saudi Basic Industries Corporation (SABIC) |
| Trademark: | SABIC® LDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | cmzSw1_SABIC-LDPE-PCG01.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
SABIC® LDPE grades for healthcare applications are produced under controlled conditions resulting in high product quality, consistency and a high level of purity. SABIC® LDPE PCG01 is an additive-free grade produced using SABIC's proprietary high pressure Clean Tubular Reactor (CTR®) which typically ensures grades with high purity. It is typically used for semi-rigid containers obtained by Blow Fill Seal (BFS) process and medical films. Compliance to Regulations SABIC® LDPE PCG01 complies with the relevant monographs of the European Pharmacopoeia (EP) and the United States Pharmacopoeia (USPVI). |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.925 | g/cm³ | ISO 1183/A |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.75 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction | 0.90 | ASTM D1894 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | ISO 527-3 | ||
| MD | 200 | MPa | |
| TD | 200 | MPa | |
| Tensile Stress | ISO 527-3 | ||
| MD : Yield | 12.0 | MPa | |
| TD : Yield | 12.0 | MPa | |
| MD : Break | 25.0 | MPa | |
| TD : Break | 20.0 | MPa | |
| Tensile Elongation | ISO 527-3 | ||
| MD : Break | > 200 | % | |
| TD : Break | > 500 | % |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Impact Strength | 150 | J/cm | ASTM D4272 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Blocking | 20 | g | Internal Method |
| Re-blocking | < 5.0 | g | Internal Method |
| Tear Strength | ISO 6383-2 | ||
| MD | 45.0 | kN/m | |
| TD | 45.0 | kN/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 98.0 | °C | ISO 306/A |
| Melting Temperature (DSC) | 113 | °C | DIN 53765 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°) | 55 | ASTM D2457 | |
| Haze | 10 | % | ASTM D1003A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sanren F500EP (1st-grade) | SINOPEC Shanghai Petrochemical Co. Ltd. | PP Random Copolymer | Sanren |
| SCHULABLEND® (ASA/PA) M/MW SF UV | A. Schulman Europe | ASA+Nylon | SCHULABLEND® |
| Sinvicomp SSZ3708 | Teknor Apex Asia Pacific PTE. LTD. | PVC, Flexible | Sinvicomp |
| ELIX™ ABS H605 | ELIX Polymers, S. L. | ABS | ELIX™ ABS |
| KOCETAL® CB301 | Kolon Plastics, Inc. | Acetal (POM) Copolymer | KOCETAL® |