SABIC® PPcompound 33MBTU
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Saudi Basic Industries Corporation (SABIC) |
| Trademark: | SABIC® PPcompound |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | cmgtMe_SABIC-PPcompound-33MBTU.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
SABIC® PPcompound 33MBTU is a 30% talc containing masterbatch for use with SABIC® PP Super high impact copolymers and as such part of the SABIC® PP CS system. This material contains UV stabilization for exterior application. SABIC® PPcompound 33MBTU is a designated automotive grade. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.15 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 40 | g/10 min | ISO 1133 |
| Molding Shrinkage (24 hr) | 0.90 | % | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2/5/50 | ||
| Yield, 3.20 mm, Injection Molded | 25.0 | MPa | |
| Break, 3.20 mm, Injection Molded | 20.0 | MPa | |
| Tensile Strain (Break, 3.20 mm, Injection Molded) | 20 | % | ISO 527-2/5/50 |
| Flexural Modulus 1(Injection Molded) | 2300 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C, Injection Molded) | 3.5 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact Strength | ISO 180/4A | ||
| -20°C, Injection Molded | 2.0 | kJ/m² | |
| 0°C, Injection Molded | 3.0 | kJ/m² | |
| 23°C, Injection Molded | 4.0 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 130 | °C | ISO 75-2/B |
| CLTE - Flow (23 to 80°C) | 8.0E-5 | cm/cm/°C | ASTM D696 |
| Note Message | |
|---|---|
| 1 . | Method I (3 point load) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TAIRIPRO F1611 | Formosa Plastics Corporation | PP Homopolymer | TAIRIPRO |
| ColorRx® TPE-OM60A0RXTP | LTL Color Compounders, Inc. | TPE | ColorRx® |
| Gallonprene® GP420-8507 | Shenzhen Sungallon Rubber & Plastic Corporation Limited | TPE | Gallonprene® |
| Polifor® C L6 GF/30 NATURALE | SO.F.TER. SPA | PP Copolymer | Polifor® |
| Sylvin 6422-62 Natural | Sylvin Technologies Incorporated | TPE | Sylvin |