Futerro® Extrusion
| Category: | PLA , Polylactic Acid |
| Manufacturer: | Futerro |
| Trademark: | Futerro® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | cm3U1L_Futerro-Extrusion.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Futerro® PLA polymer extrusion grade is a thermoplastic resin derived from annually renewable resources and is specifically designed for extrusion & thermoforming applications as, dairy containers, food service ware, transparent food containers, blister packaging, cold drink cups. Candy twist wrap, salad and Vegetable bags, window Envelope film, lidding film - Label film, Injection Stretch Blow Molded, or ISBM Bottles for 1:2 stage operations. Ideal for applications such as, Fresh Dairy, Edible Oils, Fresh Water Futerro® PLA polymer is a clear extrusion sheet grade and is easily processed on conventional extrusion and thermoforming equipment. The material is stable in the molten state, provided that the drying procedures are followed. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (25°C) | 1.24 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 190°C/2.16 kg | 2.0 - 4.0 | g/10 min | ISO 1133 |
| 210°C/2.16 kg | 5.0 - 7.0 | g/10 min | ISO 1133 |
| Free Lactide Content | % | ||
| L-poly-Lactide Content | > 99 | % | |
| Moisture Content | ppm |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3500 | MPa | ISO 527-2 |
| Tensile Stress | ISO 527-2 | ||
| Yield | 60.0 | MPa | ISO 527-2 |
| Fracture | 55.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 6.0 | % | ISO 527-2 |
| Flexural Stress | 90.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 3.5 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glass Transition Temperature | 52.0 - 60.0 | °C | ISO 11357-2 |
| Melting Temperature | 145 - 175 | °C | ISO 11357-3 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Transmittance (2000 µm) | > 90.0 | % | ISO 14782 |
| Haze (2000 µm) | < 5.0 | % | ISO 14782 |
| Fill Analysis | Nominal Value | Unit | |
|---|---|---|---|
| Melt Density (230°C) | 1.08 - 1.12 | g/cm³ |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 | °C | |
| Drying Time | 2.0 | hr | |
| Suggested Max Moisture | 0.025 | % | |
| Cylinder Zone 1 Temp. | 180 | °C | |
| Cylinder Zone 2 Temp. | 190 | °C | |
| Cylinder Zone 3 Temp. | 200 | °C | |
| Adapter Temperature | 200 | °C | |
| Melt Temperature | 210 | °C | |
| Die Temperature | 190 | °C |
| Extrusion instructions |
|---|
| Feed Throat Temperature: 45°CScrew Speed: 20 to 100 rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Resinoid 1528 | Resinoid Engineering Corporation | Phenolic | Resinoid |
| SCHULADUR® A GB 20 | A. Schulman Europe | PBT | SCHULADUR® |
| DEXFLEX® 727 | LyondellBasell Industries | TPO (POE) | DEXFLEX® |
| InnoPlus LD2420K | PTT Global Chemical Public Company Limited | LDPE | InnoPlus |
| Infino XP-2165MC | SAMSUNG SDI CO., LTD. | PPS | Infino |