TOLEN H022 CM
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | SIBUR, LLC |
| Trademark: | TOLEN |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ckq9Gl_TOLEN-H022-CM.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PP H022 CM is a polypropylene homopolymer with standard molecular mass distribution. The product features fluidity below average, a special stabilizing package including a nucleator, as well as improved physical, mechanical and thermophysical properties that enhance performance of extrusion moulding lines. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 2.0 | g/10 min | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress 1(Yield) | 30.0 | MPa | Internal Method |
| Tensile Strain 2(Yield) | 10 | % | Internal Method |
| Flexural Modulus 3 | 1500 | MPa | Internal Method |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength (23°C) | 2.0 | kJ/m² | Internal Method |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 80.0 | °C | Internal Method |
| Vicat Softening Temperature | 155 | °C | Internal Method 4 |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 5.0 mm/min |
| 4 . | A (10N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MELOPAS® MP 181 | RASCHIG GmbH | Mel Phenolic | MELOPAS® |
| TOTAL Polystyrene 879 | TOTAL Refining & Chemicals | PS (HIPS) | TOTAL Polystyrene |
| Borealis PP HG385MO | Borealis AG | PP Homopolymer | Borealis PP |
| ESTADIENE 1218 HT V0 | Cossa Polimeri S.r.l. | ABS | ESTADIENE |
| Hostacom M2 N01 L304698 | LyondellBasell Industries | PP Homopolymer | Hostacom |