Amilan® CM3004G-15
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Toray Resin Company |
| Trademark: | Amilan® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ck84qy_Amilan-CM3004G-15.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Amilan® CM3004G-15 is a Polyamide 66 (Nylon 66) product filled with 15% glass fiber. It is available in Asia Pacific, Europe, or North America. Characteristics include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Part Marking Code |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.47 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | Internal Method | |||
| Across Flow : 3.00 mm 1 | 0.80 to 1.2 | -- | % | |
| Flow : 3.00 mm 2 | 0.40 to 0.60 | -- | % | |
| Water Absorption | ISO 62 | |||
| 23°C, 24 hr | 0.40 | -- | % | |
| Saturation, 23°C | 5.0 | -- | % |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Rockwell Hardness (R-Scale, 23°C) | 120 | -- | ISO 2039-2 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Stress | ISO 527-2 | |||
| -40°C | 145 | -- | MPa | |
| 23°C | 125 | 95.0 | MPa | |
| 80°C | 60.0 | -- | MPa | |
| Tensile Strain | ISO 527-2 | |||
| Break, -40°C | 2.5 | -- | % | |
| Break, 23°C | 3.0 | 3.0 | % | |
| Break, 80°C | 4.5 | -- | % | |
| Flexural Modulus | ISO 178 | |||
| -40°C | 6200 | -- | MPa | |
| 23°C | 5700 | 3500 | MPa | |
| 80°C | 2800 | -- | MPa | |
| Flexural Stress | ISO 178 | |||
| -40°C | 200 | -- | MPa | |
| 23°C | 190 | 140 | MPa | |
| 80°C | 120 | -- | MPa | |
| Taber Abrasion Resistance (1000 Cycles) | 12.0 | -- | mg | ISO 9352 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | |||
| -40°C | 4.5 | -- | kJ/m² | |
| 23°C | 6.0 | 9.5 | kJ/m² | |
| Charpy Unnotched Impact Strength (23°C) | 40 | 48 | kJ/m² | ISO 179 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 244 | -- | °C | ISO 75-2/B |
| Melting Temperature | 265 | -- | °C | DSC |
| CLTE - Flow | 5.0E-5 | -- | cm/cm/°C | ISO 11359-2 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Volume Resistivity | 1.0E+15 | 1.0E+13 | ohms·cm | IEC 60093 |
| Electric Strength | 31 | 26 | kV/mm | IEC 60243-1 |
| Dielectric Constant 3 | IEC 60250 | |||
| 23°C, 1 kHz | 4.00 | -- | ||
| 23°C, 1 MHz | 0.0100 | -- | ||
| Arc Resistance 4 | 70.0 | -- | sec | UL 746 |
| Comparative Tracking Index (CTI) | 210 | -- | V | UL 746 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating (0.397 mm) | V-0 | -- | UL 94 |
| Note Message | |
|---|---|
| 1 . | 80x80x3 |
| 2 . | 80x80x3mm |
| 3 . | 60% RH |
| 4 . | Tungsten Electrode |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Rilsan® BMN P40 TL | Arkema | Nylon 11 | Rilsan® |
| ExxonMobil™ LLDPE LL 1004YB Film | ExxonMobil Chemical | LLDPE | ExxonMobil™ LLDPE |
| PERCOM® KAH16FR | A. Schulman Europe | PP, Unspecified | PERCOM® |
| Sylvin 9940-70 UV Yellow 4117 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| SCHULAMID® 6 MV 13 F | A. Schulman Europe | Nylon 6 | SCHULAMID® |