Bayflex® MP-10000 IMR Datasheet,PUR-Ether/MDI,Covestro

Bayflex® MP-10000 IMR

Category:	PUR-Ether/MDI , Polyurethane (Polyether, MDI)
Manufacturer:	Covestro - PUR
Trademark:	Bayflex®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	ciQDXE_Bayflex-MP-10000-IMR.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

Message
Bayflex MP-10,000 IMR is a solid elastomer which has a flexural modulus of approximately 10,000 psi (69 MPa) at room temperature. It is processed on reaction injection molding (RIM) equipment and is used for rollers, gaskets, and encapsulated windows. This system combines rapid demold times, excellent integrity at demold, improved release characteristics, and outstanding physical properties. This system also offers the advantage of an internal mold release (IMR). It is formulated to provide excellent releasability during production of RIM encapsulated windows while still maintaining strong adhesion to primed glass. Compatibility between MP-10,000 IMR and current industrial in-mold coatings is equivalent to standard Bayflex MP systems. The incorporation of internal mold release technology into RIM modular window production reduces the frequency of external mold release application. This can increase productivity by decreasing cycle time and reducing the frequency of mold cleaning. As with any product, use of the Bayflex MP-10,000 IMR system in a given application must be tested (including field testing, etc.) in advance by the user to determine suitability.

Message

Bayflex MP-10,000 IMR is a solid elastomer which has a flexural modulus of approximately 10,000 psi (69 MPa) at room temperature. It is processed on reaction injection molding (RIM) equipment and is used for rollers, gaskets, and encapsulated windows. This system combines rapid demold times, excellent integrity at demold, improved release characteristics, and outstanding physical properties.

This system also offers the advantage of an internal mold release (IMR). It is formulated to provide excellent releasability during production of RIM encapsulated windows while still maintaining strong adhesion to primed glass. Compatibility between MP-10,000 IMR and current industrial in-mold coatings is equivalent to standard Bayflex MP systems. The incorporation of internal mold release technology into RIM modular window production reduces the frequency of external mold release application. This can increase productivity by decreasing cycle time and reducing the frequency of mold cleaning. As with any product, use of the Bayflex MP-10,000 IMR system in a given application must be tested (including field testing, etc.) in advance by the user to determine suitability.

General Information
Features	Good demoulding performance
Uses	Washer Roller Doors and Windows
Forms	Liquid
Processing Method	Reaction Injection Molding (RIM)

Physical	Nominal Value	Unit	Test Method
Specific Gravity
--	0.998	g/cm³	ASTM D792
--	1.00	g/cm³	ASTM D1622
Molding Shrinkage - Flow (3.00 mm)	1.5	%	Internal method
Water Absorption (24 hr, 3.00 mm)	2.9	%	Internal method
Water absorption rate- 240 hr (3.00 mm)	5.3	%	Internal method

Thermal	Nominal Value	Unit	Test Method
Low Temperature Brittleness (-50°C, 3.00 mm)	No Cracking		ASTM D746

Additional Information	Nominal Value	Unit	Test Method
Water Immersion, Length Increase (3.00 mm)	1.5	%	Internal method

Hardness	Nominal Value	Unit	Test Method
Durometer Hardness (shaw d, 3.00mm)	40		ASTM D2240

Mechanical	Nominal Value	Unit	Test Method
Tensile Strength (Break, 3.00 mm)	15.2	MPa	ASTM D638
Flexural Modulus			ASTM D790
-30°C, 3.00 mm	183	MPa	ASTM D790
23°C, 3.00 mm	68.9	MPa	ASTM D790
65°C, 3.00 mm	53.1	MPa	ASTM D790

Elastomers	Nominal Value	Unit	Test Method
Tensile Stress			ASTM D412
20% strain ¹	4.14	MPa	ASTM D412
50% strain, 3.00mm ²	5.17	MPa	ASTM D412
100% strain, 3.00mm ³	6.89	MPa	ASTM D412
Tensile Strength (Break, 3.00 mm)	15.2	MPa	ASTM D412
Tensile Elongation (Break, 3.00 mm)	300	%	ASTM D412
Tear Strength ⁴(3.00 mm)	42.0	kN/m	ASTM D624

Thermal	Nominal Value	Unit	Test Method
CLTE - Flow (3.00 mm)	1.7E-4	cm/cm/°C	ASTM D696

Flammability	Nominal Value	Unit	Test Method
Burning Rate	15	mm/min	FMVSS 302

Thermoset	Nominal Value	Unit
Thermoset Components ⁵
Component a	Mixing ratio by weight: 39
Component B	Mixing ratio by weight: 100
Demold Time	0.50	min

Additional Information	Nominal Value	Unit	Test Method
Part A Type: Isocyanate Specific Gravity @ 25°C: 1.21 Viscosity @25°C: 700 mPa-s Flash Point PMCC: 213 °C Part B Type: Polyol Specific Gravity @ 25°C: 1.02 Viscosity @25°C: 1230 mPa-s Flash Point PMCC: 185 °C Molding Parameters Material Temperature: 35 to 45 °C Mold Temperature: 65 to 70 °C

Note Message
1 .	Die C, 510 mm/min
2 .	C mold, 510mm/min
3 .	Mouth die C, 510mm/min
4 .	C mould
5 .	105 Index

Resin Grade	Manufacturer	Category	Trademark
Telcar® TL-3050-88	Teknor Apex Company	TPE	Telcar®
THERMOLAST® M TM4LFT (Series: MC/LF)	KRAIBURG TPE	TPE	THERMOLAST® M
Multi-Pro® 3002 C	Multibase, A Dow Corning Company	PP, Unspecified	Multi-Pro®
LNP™ THERMOCOMP™ PCAF04FRHH compound	SABIC Innovative Plastics Europe	PC+ABS	LNP™ THERMOCOMP™
LGE 422	LG Polymers India Pvt. Ltd.	PS (EPS)	LGE

Resin Grade

Manufacturer