Order Products : sales@su-jiao.com
OmniCarb鈩?PC GR10
| Category: | PC , Polycarbonate |
| Manufacturer: | OMNI Plastics, LLC |
| Trademark: | OmniCarb™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | chf1Rp_OmniCarb-PC-GR10.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 10% Glass Reinforced Polycarbonate |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.25 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 14 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield, 23°C) | 62.1 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 5.0 | % | ASTM D638 |
| Flexural Modulus | 2960 | MPa | ASTM D790 |
| Flexural Strength | 82.7 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 170 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 3.18 mm | 138 | °C | |
| 1.8 MPa, Unannealed, 3.18 mm | 135 | °C |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (3.00 mm) | HB | Internal Method |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 249 to 293 | °C | |
| Middle Temperature | 271 to 304 | °C | |
| Front Temperature | 271 to 304 | °C | |
| Nozzle Temperature | 271 to 304 | °C | |
| Processing (Melt) Temp | 271 to 304 | °C | |
| Mold Temperature | 48.9 to 104 | °C | |
| Back Pressure | 0.172 to 0.345 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SPESIN® KP212G15V0WH | Kolon Plastics, Inc. | PBT | SPESIN® |
| TULAMID® PA-SV30-LT2 | UCC Shchekinoazot | Nylon 6 | TULAMID® |
| Nylene® 4114-14 | Custom Resins Group | Nylon 66 | Nylene® |
| Chemlon® 233 GVH | Teknor Apex Company (Chem Polymer) | Nylon 6 | Chemlon® |
| Fainplast PVC PH 45/N | Fainplast Compounds S.r.l | PVC, Flexible | Fainplast PVC |