POLYelast TPE 10012 R3
| Category: | PP+EPDM , Polypropylene + EPDM Rubber |
| Manufacturer: | Polykemi AB |
| Trademark: | POLYelast |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | cgrtIv_POLYelast-TPE-10012-R3.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PP/Elastomer Mineral reinforced |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.980 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 10 | g/10 min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow | 0.80 to 1.0 | % | |
| Flow | 0.80 to 1.0 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | 18.0 | MPa | ISO 527-2 |
| Tensile Strain | ISO 527-2 | ||
| Yield | 10 | % | |
| Break | 200 | % | |
| Flexural Modulus (23°C) | 1100 | MPa | ISO 178 |
| Flexural Stress | 25.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -20°C | 28 | kJ/m² | |
| 23°C | 30 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179 | ||
| -20°C | No Break | ||
| 23°C | No Break |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 1 | |||
| 0.45 MPa, Unannealed | 95.0 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 45.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 124 | °C | ISO 306/A50 |
| -- | 50.0 | °C | ISO 306/B50 |
| CLTE - Flow | 6.0E-5 to 8.0E-5 | cm/cm/°C | Internal Method |
| Note Message | |
|---|---|
| 1 . | 120°C/hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| 4LEX® 25F23100 | 4Plas | PC | 4LEX® |
| NYLOY® UB-0010N G35L1N | Nytex Composites Co., Ltd. | Nylon, Unspecified | NYLOY® |
| Bayblend® FR1514 BBS073 | Covestro - Polycarbonates | PC+ABS | Bayblend® |
| Kpren 130A | Shandong Xuye New Materials Co., Ltd. | CPE | Kpren |
| Osterlene® PPC-20-2.0-A | Osterman & Company | PP Impact Copolymer | Osterlene® |