LNP™ LUBRICOMP™ KI001XXJ compound
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | cgisQ2_LNP-LUBRICOMP-KI001XXJ-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP KI001XXJ is a compound based on Acetal containing 2% Silicone. Added features of this grade include: Wear Resistant, Healthcare. Also known as: LNP* LUBRICOMP* Compound KL-4410 HC Product reorder name: KI001XXJ |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.40 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 2.4 | % | |
| Across Flow : 24 hr | 2.4 | % | |
| Water Absorption (24 hr, 50% RH) | 0.24 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 2750 | MPa | ASTM D638 |
| Tensile Strength 2 | ASTM D638 | ||
| Yield | 55.0 | MPa | |
| Break | 52.0 | MPa | |
| Tensile Elongation 3 | ASTM D638 | ||
| Yield | 16 | % | |
| Break | 46 | % | |
| Flexural Modulus 4(50.0 mm Span) | 2280 | MPa | ASTM D790 |
| Flexural Strength 5(Yield, 50.0 mm Span) | 74.7 | MPa | ASTM D790 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| vs. Itself - Dynamic | 0.44 | ||
| vs. Itself - Static | 0.34 | ||
| Wear Factor - Washer | 22.0 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 82 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 1600 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.20 mm) | 106 | °C | ASTM D648 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 177 to 188 | °C | |
| Middle Temperature | 193 to 204 | °C | |
| Front Temperature | 210 to 221 | °C | |
| Processing (Melt) Temp | 199 to 216 | °C | |
| Mold Temperature | 82.2 to 110 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Gallonprene® GP420-7502 | Shenzhen Sungallon Rubber & Plastic Corporation Limited | TPE | Gallonprene® |
| EMOPLEN® HP MCF 20 | EMAS Plastik San.Tic.AS. | PP Homopolymer | EMOPLEN® |
| KumhoSunny PBT/ABS HAB8740 | Shanghai KumhoSunny Plastics Co., Ltd. | ABS+PBT | KumhoSunny PBT/ABS |
| Pearlbond™ 125H | Lubrizol Advanced Materials, Inc. | TPU-Polyester | Pearlbond™ |
| NEOFLON™ NP-30 | DAIKIN AMERICA, INC. | FEP | NEOFLON™ |