Zytel® 80G14A NC010A
| Category: | Nylon 66 , NYLON RESIN |
| Manufacturer: | DuPont Performance Polymers |
| Trademark: | Zytel® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | cggvY6_Zytel-80G14A-NC010A.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 14% Glass Reinforced, Toughened, Polyamide 66 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Forms |
|
| Processing Method |
|
| Multi-Point Data |
|
| Part Marking Code (ISO 11469) |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.19 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow | 0.80 | -- | % | |
| Flow | 0.70 | -- | % | |
| Water Absorption | ISO 62 | |||
| 23°C, 24 hr, 2.00 mm | 6.2 | -- | % | |
| Equilibrium, 23°C, 2.00 mm, 50% RH | 1.8 | -- | % | |
| Viscosity Number | 137 | -- | cm³/g | ISO 307 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 4800 | 3400 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 108 | 66.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 3.8 | 10 | % | ISO 527-2 |
| Tensile Creep Modulus | ISO 899-1 | |||
| 1 hr | -- | 3100 | MPa | |
| 1000 hr | -- | 2500 | MPa | |
| Flexural Modulus | 4400 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -40°C | -- | 6.0 | kJ/m² | |
| -30°C | 10 | 7.0 | kJ/m² | |
| 23°C | 13 | 17 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 90 | 71 | kJ/m² | |
| 23°C | 70 | 76 | kJ/m² | |
| Notched Izod Impact Strength | ISO 180/1A | |||
| -40°C | 6.0 | -- | kJ/m² | |
| 23°C | 13 | -- | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 258 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 240 | -- | °C | ISO 75-2/A |
| Vicat Softening Temperature | 215 | -- | °C | ISO 306/B50 |
| Melting Temperature 1 | 263 | -- | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | |||
| Flow | 4.0E-5 | -- | cm/cm/°C | |
| Transverse | 1.2E-4 | -- | cm/cm/°C |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | -- | 1.0E+14 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+15 | 1.0E+12 | ohms·cm | IEC 60093 |
| Electric Strength | 36 | 37 | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | |||
| 100 Hz | 3.80 | 7.30 | ||
| 1 MHz | 3.50 | 3.90 | ||
| Dissipation Factor | IEC 60250 | |||
| 100 Hz | 0.027 | 0.018 | ||
| 1 MHz | 0.058 | 0.058 | ||
| Comparative Tracking Index | 600 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Burning Rate 2(1.00 mm) | 44 | -- | mm/min | ISO 3795 |
| Flammability Classification | IEC 60695-11-10, -20 | |||
| 0.750 mm | HB | -- | ||
| 1.50 mm | HB | -- |
| Fill Analysis | Dry | Conditioned | Unit | |
|---|---|---|---|---|
| Specific Heat Capacity of Melt | 2350 | -- | J/kg/°C | |
| Thermal Conductivity of Melt | 0.19 | -- | W/m/K |
| Additional Information | Dry | Conditioned | Unit | |
|---|---|---|---|---|
| Effective Thermal Diffusivity | 0.0809 | -- | cSt |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| 2 . | DS |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxxam™ DC-818.G001-8000 | PolyOne Corporation | PP, Unspecified | Maxxam™ |
| TROGAMID® Care MX97 | Evonik Industries AG | Nylon, Unspecified | TROGAMID® Care |
| Formolene® L62009B | Formosa Plastics Corporation, U.S.A. | LLDPE | Formolene® |
| Panlite® ML-1103 | TEIJIN LIMITED | PC | Panlite® |
| Maxxam™ PP5120F B2 | PolyOne Corporation | PP Homopolymer | Maxxam™ |