COSMOPLENE® AW564

Category: PP Copolymer , Polypropylene Copolymer
Manufacturer: TPC, The Polyolefin Company (Singapore) Pte Ltd
Trademark: COSMOPLENE®
Fillers: -
Ports: Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms FOB, CIF, DAP, DAT, DDP
PDF: cfN4r0_COSMOPLENE-AW564.pdf
PRICE: ​Order Products​ email   sales@su-jiao.com
Wechat: WECHAT
Message
COSMOPLENE AW564 is high impact PP copolymer manufactured by gas phase process licensed from Sumitomo Chemical Co. Japan.

COSMOPLENE AW564 is medium flow, high stiffness, high impact copolymer grade.

COSMOPLENE AW564 is specially designed for crate and base for washing machine etc.
General Information
Features
  • High Impact Resistance
  • High Stiffness
  • Impact Copolymer
  • Medium Flow
Uses
  • Appliance Components
  • Crates
UL File Number
  • E108370
Forms
  • Pellets
PhysicalNominal ValueUnitTest Method
Specific Gravity 0.900g/cm³ASTM D792
Melt Mass-Flow Rate (MFR) 9.0g/10 minASTM D1238
Molding Shrinkage Internal Method
    Flow : 2.00 mm 1.6%
    Across Flow : 2.00 mm 1.7%
HardnessNominal ValueUnitTest Method
Rockwell Hardness (R-Scale)91ASTM D785
MechanicalNominal ValueUnitTest Method
Tensile Strength ASTM D638
    Yield 27.5MPa
    Break 23.0MPa
Tensile Elongation (Break)300%ASTM D638
Flexural Modulus 1290MPaASTM D790
ImpactNominal ValueUnitTest Method
Notched Izod Impact ASTM D256
    -20°C 45J/m
    23°C 92J/m
ThermalNominal ValueUnitTest Method
Deflection Temperature Under Load (0.45 MPa, Unannealed)124°CASTM D648
FlammabilityNominal ValueTest Method
Flame Rating HBUL 94
InjectionNominal ValueUnit
Rear Temperature 190 to 230°C
Middle Temperature 190 to 230°C
Front Temperature 190 to 230°C
Mold Temperature 30.0°C
Injection Pressure 6.86MPa
Clamp Tonnage 0.98kN/cm²
Resin Grade Manufacturer Category Trademark
SCLAIR® 58A NOVA Chemicals HDPE SCLAIR®
TEKNIFLEX® PTA2200 Tekni-Films, a div of Tekni-Plex Film, PE/PCTFE TEKNIFLEX®
XYRON™ L544V Asahi Kasei Chemicals Corporation PPE+PS XYRON™
Hiprolon® 400 FN Arkema Nylon 1012 Hiprolon®
LNP™ LUBRICOMP™ SCP36 compound SABIC Innovative Plastics Nylon 12 LNP™ LUBRICOMP™