DOW™ LDPE 352E

Category:	LDPE , Low Density Polyethylene Resin
Manufacturer:	The Dow Chemical Company
Trademark:	DOW™ LDPE
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	cfCHCZ_DOW-LDPE-352E.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

DOW LDPE 352E Low Density Polyethylene Resin is a high clarity resin designed for clarity over wrap applications. This resin does contain erucamide slip and antiblock additives. It can be readily extruded using conventional blown film techniques utilising melt temperatures between 160 and 175 °C.

This resin when properly fabricated exhibits:

Excellent processability and draw drown.

Outstanding toughness and impact properties.

Superior optical properties.

Excellent tensile and tear strength.

Applications:

Light-produce bags.

Soft goods packaging.

Textile packaging.

Good optical general purpose bags.

Hygiene films.

Food packaging films.

Complies with:

CANADIAN HPFB NO OBJECTION (WITH LIMITATIONS)

EU, No 10/2011

U.S. FDA 21 CFR 177.1520(c)2.2

Consult the regulations for complete details.

General Information
Additive	Erucamide Lubricating Additive Anti-caking agent
Agency Ratings	FDA 21 CFR 177.1520 HPFB (Canada) No Objection Europe No 10/2011
Forms	Particle

Physical	Nominal Value	Unit	Test Method
Specific Gravity	0.925	g/cm³	ASTM D792
Melt Mass-Flow Rate (MFR) (190°C/2.16 kg)	2.0	g/10 min	ISO 1133

Mechanical	Nominal Value	Unit	Test Method
Coefficient of Friction (vs. Itself - Dynamic)	0.15 - 0.20		ASTM D1894

Films	Nominal Value	Unit	Test Method
Film Thickness - Tested	50	µm
secant modulus			ASTM D882
2% secant, MD : 50 µm	190	MPa	ASTM D882
2% secant, TD : 50 µm	210	MPa	ASTM D882
Tensile Strength			ASTM D882
MD : Yield, 50 µm	10.0	MPa	ASTM D882
TD : Yield, 50 µm	11.0	MPa	ASTM D882
MD : Break, 50 µm	22.0	MPa	ASTM D882
TD : Break, 50 µm	20.0	MPa	ASTM D882
Tensile Elongation			ASTM D882
MD : Break, 50 µm	450	%	ASTM D882
TD : Break, 50 µm	650	%	ASTM D882
Dart Drop Impact (50 µm)	110	g	ASTM D1709A
Elmendorf Tear Strength			ASTM D1922
MD : 50 µm	450	g	ASTM D1922
TD : 50 µm	350	g	ASTM D1922

Thermal	Nominal Value	Unit	Test Method
Vicat Softening Temperature	96.0	°C	ISO 306/A

Optical	Nominal Value	Unit	Test Method
Gloss (20°, 50.0 µm)	60		ASTM D2457
Haze (50.0 µm)	8.0	%	ASTM D1003

Extrusion	Nominal Value	Unit
Melt Temperature	160 - 175	°C

Extrusion instructions
薄膜放大比 1:2.5

Resin Grade	Manufacturer	Category	Trademark
MARPOL® LL4F 801-SB	Marco Polo International, Inc.	LLDPE	MARPOL®
TABOREX TA 1135 HD	SILON s.ro	HDPE	TABOREX
TOTAL Polystyrene Compound 818R	TOTAL Refining & Chemicals	PS (Specialty)	TOTAL Polystyrene
Nanguang TPU Y-80AX	Fujian Nanguang Light Industry Co., Ltd.	TPU, Unspecified	Nanguang TPU
Diakon® ST35N8	Lucite International Inc.	Acrylic (PMMA)	Diakon®