K-Prene D S 572
| Category: | MPR , Melt Processable Rubber |
| Manufacturer: | Technovinyl Polymers India Ltd. |
| Trademark: | K-Prene |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | cekh87_K-Prene-D-S-572.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
K-Prene D S 572 is a Melt Processable Rubber (MPR) material. It is available in Africa & Middle East. Typical application of K-Prene D S 572: Consumer Goods |
| General Information | |
|---|---|
| Uses |
|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.960 | g/cm³ | DIN 53479 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 200°C/2.16 kg | 20 | g/10 min | |
| 200°C/5.0 kg | 80 | g/10 min |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A) | 57 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 6.86 | MPa | ASTM D638 |
| Abrasion | 170 | mm/kc | DIN 53516 |
| Additional Information | Nominal Value | Test Method | |
|---|---|---|---|
| Cut Growth - Flex Resistance 1(20°C, 9.00 cm) | < 0.100 | Internal Method |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 7.85 | MPa | ASTM D412 |
| Tensile Elongation (Break) | 1000 | % | ASTM D412 |
| Tear Strength | 50.0 | kN/m | DIN 53515 |
| Note Message | |
|---|---|
| 1 . | 120000 cycle, |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Resinoid 2215 | Resinoid Engineering Corporation | Phenolic | Resinoid |
| TAROPRENE® 1 A80 E1N | Taro Plast S.p.A. | TPV | TAROPRENE® |
| KRATON® G1652 H | Kraton Polymers LLC | SEBS | KRATON® |
| Karina BLUE PVC COMP. -E 851-06/347-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LubX® C pressed | Röchling Engineering Plastics SE & Co. KG | UHMWPE | LubX® |