Petrothene® NA373244
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Petrothene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ceMrUO_Petrothene-NA373244.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Petrothene NA373 is a series of homopolymer resins selected by customers for use in household film and other applications that require high clarity and good impact strength combined with low COF. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.924 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 3.0 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 32 | µm | |
| Secant Modulus | ASTM D882 | ||
| 1% Secant, MD : 32 µm, Blown Film | 159 | MPa | |
| 1% Secant, MD : 32 µm, Cast Film | 208 | MPa | |
| 1% Secant, TD : 32 µm, Blown Film | 172 | MPa | |
| 1% Secant, TD : 32 µm, Cast Film | 197 | MPa | |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 32 µm, Blown Film | 10.9 | MPa | |
| MD : Yield, 32 µm, Cast Film | 9.38 | MPa | |
| TD : Yield, 32 µm, Blown Film | 10.7 | MPa | |
| TD : Yield, 32 µm, Cast Film | 9.31 | MPa | |
| MD : Break, 32 µm, Blown Film | 18.6 | MPa | |
| MD : Break, 32 µm, Cast Film | 29.1 | MPa | |
| TD : Break, 32 µm, Blown Film | 17.2 | MPa | |
| TD : Break, 32 µm, Cast Film | 17.0 | MPa | |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 32 µm, Blown Film | 200 | % | |
| MD : Break, 32 µm, Cast Film | 230 | % | |
| TD : Break, 32 µm, Blown Film | 500 | % | |
| TD : Break, 32 µm, Cast Film | 610 | % | |
| Dart Drop Impact | ASTM D1709 | ||
| 32 µm, Blown Film | 65 | g | |
| 32 µm, Cast Film | 110 | g | |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 32 µm, Blown Film | 270 | g | |
| MD : 32 µm, Cast Film | 300 | g | |
| TD : 32 µm, Blown Film | 170 | g | |
| TD : 32 µm, Cast Film | 160 | g |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss | ASTM D2457 | ||
| 45°, 31.8 µm, Blown Film | 70 | ||
| 45°, 31.8 µm, Cast Film | 77 | ||
| Haze | ASTM D1003 | ||
| 31.8 µm, Blown Film | 5.4 | % | |
| 31.8 µm, Cast Film | 3.4 | % |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ARCEL® ULV (1.5 pcf) | NOVA Chemicals | PS+PE | ARCEL® |
| Hapflex™ 595-3 | Hapco Inc. | TP, Unspecified | Hapflex™ |
| ISOTHANE® 1080A | Great Eastern Resins Industrial Co Ltd (GRECO) | TPU-Polyester | ISOTHANE® |
| LNP™ LUBRICOMP™ DL003EU compound | SABIC Innovative Plastics | PC | LNP™ LUBRICOMP™ |
| Plenco 02408 (Injection) | Plastics Engineering Co. | Phenolic | Plenco |