EVAL™ SP292
| Category: | EVOH , Ethylene Vinyl Alcohol |
| Manufacturer: | Kuraray Co., Ltd. |
| Trademark: | EVAL™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ceCvWz_EVAL-SP292.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| High Orientability Ethylene Vinyl Alcohol Copolymer Applications: Shrink Film, Skin Packaging and thermoforming |
| General Information | |
|---|---|
| Uses |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.13 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 190°C/2.16 kg | 2.0 | g/10 min | ISO 1133 |
| 210°C/2.16 kg | 4.5 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2300 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 25.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 17 | % | ISO 527-2 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Oxygen Permeability | ISO 14663-2 | ||
| 20°C, 65% RH | 0.035 | cm³·mm/m²/atm/24 hr | ISO 14663-2 |
| 20°C, 85% RH | 0.085 | cm³·mm/m²/atm/24 hr | ISO 14663-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glass Transition Temperature | 48.0 | °C | ISO 11357-2 |
| Melting Temperature | 161 | °C | ISO 11357 |
| Peak Crystallization Temperature | 141 | °C | ISO 11357-3 |
| Additional Information |
|---|
| Limit of Orientability, Simultaneous, Kuraray Method: 4.5 x 4.5 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Dryflex® 660450S | ELASTO | SEBS | Dryflex® |
| Hifax CA 1110 G4 | LyondellBasell Industries | PP Impact Copolymer | Hifax |
| Karina STRAW PVC COMPOUND 800-38/39-A-ERYB | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| SIBUR Synthetic Rubber SSBR-2560 Grade C | SIBUR | SBR, Solution | SIBUR Synthetic Rubber |
| POTICON NT363 | Otsuka Chemical Co., Ltd. | Nylon, Unspecified | POTICON |