Koattro KT MR 05

Category:	POP , Polyolefin Plastomer
Manufacturer:	LyondellBasell Industries
Trademark:	Koattro
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	cdxnHA_KoattroKTMR05.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

Koattro KT MR05 is a novel plastomeric material based on Lyondellbasell technology with unique characteristics and is highly compatible with Polypropylene(PP).

This product blended with PP enhances softness, elastic recovery, elongation at break and impact resistance whilst improving transparancy and reducing stress whitening.

Koattro KT MR05 is available in free flowing pellet form.

This product is not intended for use in medical and pharmaceutical applications.

General Information
Features	Resilient recovery, excellent Flexibility at low temperatures High elasticity Foamable property Weldable Good processing stability Good melt strength Medium liquidity
Uses	Blown Film Films Electrical appliances Industrial application cast film Sealant Application in Automobile Field Automotive exterior parts Color masterbatch Plastic modification Coating application
Forms	Particle
Processing Method	Spunbond Nonwovens Blow film Extrusion cast film Filament extrusion Fiber (spinning) extrusion Compression molding Calendering Injection molding

Physical	Nominal Value	Unit	Test Method
Density	0.870	g/cm³	ISO 1183
Melt Mass-Flow Rate (MFR) (190°C/2.16 kg)	1.0	g/10 min	ISO 1133

Hardness	Nominal Value	Unit	Test Method
Durometer Hardness (Shore A)	60		ISO 868

Mechanical	Nominal Value	Unit	Test Method
Tensile Stress ¹(Break, Compression Molded)	12.0	MPa	ISO 8986-2
Tensile Strain ²(Break, Compression Molded)	> 800	%	ISO 8986-2
Flexural Modulus ³(23°C)	< 10.0	MPa	ISO 178

Elastomers	Nominal Value	Unit	Test Method
Compression Set ⁴(23°C)	30	%	ASTM D395

Impact	Nominal Value	Unit	Test Method
Charpy Notched Impact Strength (-20°C)	No Break		ISO 179

Extrusion	Nominal Value	Unit
Melt Temperature	200 - 260	°C

Note Message
1 .	Type IV, Conditioned for 10 days at 20°C
2 .	Type IV, Conditioned for 10 days at 20°C
3 .	Conditioned for 10 days at 20°C
4 .	25% deformation

Resin Grade	Manufacturer	Category	Trademark
Sarlink® TPV 3139DN	Teknor Apex Company	TPV	Sarlink® TPV
Sindustris PP HG3201SK2	Sincerity Australia Pty Ltd.	PP, Unspecified	Sindustris PP
TAROLOX GFR	Taro Plast S.p.A.	PBT	TAROLOX
Karina WHITE PVC COMPOUND -E 800-10/194-Y-CRB	Karina Ind. e Com. de Plásticos Ltda	PVC, Unspecified	Karina
DEXFLEX® 815 BLK XXX	LyondellBasell Industries	TPO (POE)	DEXFLEX®