DENKA Transparent Polymer TE-20S
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Denka Company Limited |
| Trademark: | DENKA Transparent Polymer |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | cdhX65_DENKA-Transparent-Polymer-TE-20S.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
DENKA Transparent Polymer TE-20S is an Acrylonitrile Butadiene Styrene (ABS) product. It can be processed by injection molding and is available in Asia Pacific, Europe, or North America. Characteristics include:
|
| General Information | |
|---|---|
| Features |
|
| UL File Number |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.11 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 200°C/5.0 kg | 2.0 | g/10 min | |
| 220°C/10.0 kg | 28 | g/10 min | |
| Molding Shrinkage (2.00 mm) | 0.50 | % | Internal Method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 54 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 48.0 | MPa | ISO 527-2/50 |
| Nominal Tensile Strain at Break | 34 | % | ISO 527-2/50 |
| Flexural Modulus 1 | 2300 | MPa | ISO 178 |
| Flexural Stress 2 | 74.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 10 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 73.0 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | 93.0 | °C | ISO 306/B |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Transmittance (2000 µm) | 91.0 | % | ISO 13468-1 |
| Haze (2000 µm) | 1.3 | % | ISO 14782 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 to 3.0 | hr | |
| Rear Temperature | 200 to 240 | °C | |
| Middle Temperature | 200 to 240 | °C | |
| Front Temperature | 200 to 240 | °C | |
| Nozzle Temperature | 230 to 240 | °C | |
| Mold Temperature | 40.0 to 70.0 | °C |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYLON IR 1900 | POLYMA Kunststoff GmbH & Co. KG | PC | POLYLON |
| Cri-Line LC-815-85 | Cri-Tech, Inc. | Fluorelastomer | Cri-Line |
| Edgetek™ EM01042076BG | PolyOne Corporation | PC | Edgetek™ |
| Eltex® A4009PFN1324 | INEOS Olefins & Polymers Europe | HDPE | Eltex® |
| Sylvin 8940-70 NATURAL | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |