FLEXITEQ™ F65A100
| Category: | TPV , Thermoplastic Vulcanizate |
| Manufacturer: | Marplex Australia Pty. Ltd. |
| Trademark: | FLEXITEQ™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | cdRS5E_FLEXITEQ-F65A100.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| FLEXITEQ™ F65A100 is a formulation based on Santoprene™ rubber technology. It is formulated to incorporate soft-touch and good mouldability. FLEXITEQ™ F65A100 can be processed on conventional thermoplastic equipment for injection moulding. It is polyolefin based and completely recyclable. |
| General Information | |
|---|---|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.968 | g/cm³ | ASTM D792 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A, 15 sec) | 70 | ASTM D2240 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Break) | 5.20 | MPa | ASTM D412 |
| Tensile Elongation 2(Break) | 330 | % | ASTM D412 |
| Tear Strength 3(23°C) | 28.0 | kN/m | ASTM D624 |
| Compression Set 4(23°C, 70 hr) | 35 | % | ASTM D395B |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 - 85.0 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Rear Temperature | 160 - 190 | °C | |
| Middle Temperature | 180 - 210 | °C | |
| Front Temperature | 190 - 210 | °C | |
| Processing (Melt) Temp | 190 - 210 | °C | |
| Mold Temperature | 10.0 - 80.0 | °C | |
| Injection Rate | Fast | ||
| Back Pressure | 0.300 - 0.700 | MPa | |
| Screw Speed | 100 - 200 | rpm | |
| Clamp Tonnage | 3.0 - 5.0 | kN/cm² |
| Injection instructions |
|---|
| Injection Pressure: High |
| Note Message | |
|---|---|
| 1 . | C mold, 500 mm/min |
| 2 . | Mouth die C, 500 mm/min |
| 3 . | C mold, 500 mm/min |
| 4 . | Type 2 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Badalac® ABS 30 | Bada AG | ABS | Badalac® |
| Edgetek™ AT-1000 | PolyOne Corporation | Acetal (POM) Copolymer | Edgetek™ |
| Kingfa PP-116 | Kingfa | PP, Unspecified | Kingfa |
| Lupoy® 3010-15 | LG Chem Ltd. | PC | Lupoy® |
| Sylvin 5132-75 Clear Green 3157 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |