Starpylen MF008S
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Eurostar Engineering Plastics |
| Trademark: | Starpylen |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | cdENxk_Starpylen-MF008S.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Starpylen MF008S is 40% Glass Fiber Reinforced Polypropylene Injection Molding Resin |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.22 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow (24 hr) | 0.20 to 0.40 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Break) | 87.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 2.7 | % | ISO 527-2/5 |
| Flexural Modulus 1 | 6800 | MPa | ISO 178 |
| Flexural Stress | 129 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength 2(23°C) | 10 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 3(1.8 MPa, Unannealed, 64.0 mm Span) | 142 | °C | ISO 75-2/Af |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.00 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 | °C | |
| Drying Time | 3.0 | hr | |
| Rear Temperature | 195 to 205 | °C | |
| Middle Temperature | 215 to 225 | °C | |
| Front Temperature | 225 to 250 | °C | |
| Processing (Melt) Temp | 225 to 250 | °C | |
| Mold Temperature | 30.0 to 50.0 | °C |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Razalen® R123 TR15 | Razin™ Engineering Plastics | PP+EPDM | Razalen® |
| Quantum Composites QC-8565 | Quantum Composites Inc. | Vinyl Ester | Quantum Composites |
| Staramide BG6 | Eurostar Engineering Plastics | Nylon 6 | Staramide |
| WELLAMID Nylon 6000 CF 10 HWCP | CP-Polymer-Technik GmbH & Co. KG | Nylon 6 | WELLAMID Nylon |
| LONGLITE® PBT 3050-104X | CCP Group | PBT | LONGLITE® PBT |