FORMULA P COMP 3525 GB M1
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Putsch Kunststoffe GmbH |
| Trademark: | FORMULA P |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | cdBY2G_FORMULA-P-COMP-3525-GB-M1.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Mineral and glass fiber reinforced. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.07 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 10 | g/10 min | ISO 1133 |
| Molding Shrinkage | 0.60 - 1.0 | % | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2 | ||
| Yield | 24.0 | MPa | ISO 527-2 |
| Fracture | 27.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 10 | % | ISO 527-2 |
| Flexural Modulus | 2300 | MPa | ISO 178 |
| Flexural Stress (3.5% Strain) | 60.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 5.0 | kJ/m² | ISO 180 |
| Additional Information |
|---|
| Tensile Strength, ISO 527: 25 MPa |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 | hr | |
| Processing (Melt) Temp | 245 - 265 | °C | |
| Mold Temperature | 40.0 - 60.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Rhelon F2038H-01 | RheTech, Inc. | Nylon 66 | Rhelon |
| LNP™ THERMOCOMP™ UCF22S compound | SABIC Innovative Plastics | PPA | LNP™ THERMOCOMP™ |
| Polifor® L6 GF/20 NATURALE | SO.F.TER. SPA | PP Homopolymer | Polifor® |
| Axiall PVC 7465A | Axiall Corporation | PVC, Rigid | Axiall PVC |
| PERSTIR® B43K7000AH0 | A.D. Compound S.p.A. | PS (GPPS) | PERSTIR® |