NORYL™ SE100X resin
| Category: | PPE+PS , Polyphenylene Ether + PS |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | NORYL™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | caimtn_NORYLSE100Xresin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Nonbrominated, nonchlorinated FR resin. Improved productivity and reliability. 199F HDT. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.10 | g/cm³ | ASTM D792 |
| Molding Shrinkage | Internal method | ||
| Flow : 3.20mm | 0.50 - 0.70 | % | Internal method |
| Transverse flow 1 | 0.50 - 0.70 | % | Internal method |
| Outdoor Suitability | f1 | UL 746C |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 2 | ASTM D638 | ||
| Yield | 57.9 | MPa | ASTM D638 |
| Fracture | 46.9 | MPa | ASTM D638 |
| Tensile Elongation 3 | ASTM D638 | ||
| Yield | 6.5 | % | ASTM D638 |
| Fracture | 25 | % | ASTM D638 |
| Flexural Modulus 4(100 mm Span) | 2310 | MPa | ASTM D790 |
| Flexural Strength 5(Yield, 100 mm Span) | 82.7 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -30°C | 91 | J/m | ASTM D256 |
| 23°C | 260 | J/m | ASTM D256 |
| Instrumented Dart Impact | ASTM D3763 | ||
| -30°C, Energy at Peak Load | 16.3 | J | ASTM D3763 |
| 23°C, Energy at Peak Load | 40.7 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, unannealed, 6.40mm | 102 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 6.40mm | 92.8 | °C | ASTM D648 |
| RTI Elec | 95.0 | °C | UL 746 |
| RTI Imp | 80.0 | °C | UL 746 |
| RTI | 95.0 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | ohms | ASTM D257 |
| Volume Resistivity | 3.1E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength (3.20 mm, in Oil) | 18 | kV/mm | ASTM D149 |
| Dielectric Constant | ASTM D150 | ||
| 50 Hz | 2.66 | ASTM D150 | |
| 60 Hz | 2.66 | ASTM D150 | |
| 1 MHz | 2.57 | ASTM D150 | |
| Dissipation Factor | ASTM D150 | ||
| 50 Hz | 6.0E-3 | ASTM D150 | |
| 60 Hz | 6.0E-3 | ASTM D150 | |
| 1 MHz | 2.6E-3 | ASTM D150 | |
| Arc Resistance 6 | PLC 7 | ASTM D495 | |
| Comparative Tracking Index (CTI) | PLC 1 | UL 746 | |
| High Voltage Arc Tracking Rate (HVTR) | PLC 4 | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.47 mm | V-1 | UL 94 | |
| 5.99 mm | V-0 | UL 94 | |
| Oxygen Index | 33 | % | ASTM D2863 |
| Radiant Panel Listing (UL) | YES |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 76.7 - 82.2 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 30 - 70 | % | |
| Rear Temperature | 216 - 266 | °C | |
| Middle Temperature | 227 - 271 | °C | |
| Front Temperature | 238 - 277 | °C | |
| Nozzle Temperature | 249 - 277 | °C | |
| Processing (Melt) Temp | 249 - 277 | °C | |
| Mold Temperature | 54.4 - 76.7 | °C | |
| Back Pressure | 0.345 - 0.689 | MPa | |
| Screw Speed | 20 - 100 | rpm | |
| Vent Depth | 0.038 - 0.051 | mm |
| Note Message | |
|---|---|
| 1 . | Tensile Bar |
| 2 . | Type 1, 50mm/min |
| 3 . | Type 1, 50mm/min |
| 4 . | 2.6 mm/min |
| 5 . | 2.6 mm/min |
| 6 . | Tungsten electrode |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sinpolene TPP2030 | Teknor Apex Asia Pacific PTE. LTD. | PP Copolymer | Sinpolene |
| Sup-tech B230 | Shanghai Suptech Engineering Plastics Co. Ltd. | Nylon 6 | Sup-tech |
| Adiprene® Duracast® C930 | Chemtura | PUR-Capro/MDI | Adiprene® Duracast® |
| HiFill® POM HO 0167 S1 | Techmer Engineered Solutions | Acetal (POM) Copolymer | HiFill® |
| Lucel® HI510 | LG Chem Ltd. | Acetal (POM) Copolymer | Lucel® |