Devcon Dev-Thane™ 5
| Category: | PUR, Unspecified , Polyurethane |
| Manufacturer: | Devcon |
| Trademark: | Devcon |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | cadPVE_Devcon-Dev-Thane-5.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
A two-part, fast setting. Primerless high performance urethane adhesive for bonding many different substrates such as steel, aluminium, ABS, urethane, and composites. Intended Use:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Volume | 0.708 | cm³/g | |
| Solid content- by Volume | 100 | % |
| Thermal | Nominal Value | Unit | |
|---|---|---|---|
| Service Temperature | -40 - 93 | °C |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Work Time (24°C) | 5.0 | min |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Shear Adhesion | ASTM D1002 | ||
| ABS | 4.34 | MPa | ASTM D1002 |
| AL | 8.76 | MPa | ASTM D1002 |
| Concrete | 8.27 | MPa | ASTM D1002 |
| Galvanized mtl | 10.9 | MPa | ASTM D1002 |
| GBS | 19.0 | MPa | ASTM D1002 |
| SMC | 6.17 | MPa | ASTM D1002 |
| SS | 12.7 | MPa | ASTM D1002 |
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density 1 | 1.41 | g/cm³ | |
| Molding Shrinkage - Flow | 0.14 | % | ASTM D2566 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 63 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 14.5 | MPa | ASTM D638 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Elongation (Break) | 200 | % | ASTM D412 |
| Tear Strength | 70.1 | kN/m | ASTM D624 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength | 14 | kV/mm | ASTM D149 |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Components | |||
| Component a | Mixing ratio by weight: 1.0 Mixing ratio by capacity: 1.0 | ||
| Component B | Mixing ratio by weight: 1.0 Mixing ratio by capacity: 1.0 | ||
| Shelf Life | 52 | wk | |
| Thermoset Mix Viscosity | 45000 | cP |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Cured 7 days @ 75°F |
| Uncured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Curing Time | 24 | hr |
| Note Message | |
|---|---|
| 1 . | Mixed |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 881 TFE 10 SI 2 | RTP Company | Acetal (POM) Copolymer | RTP |
| Sylvin 8696-70 Clear 876 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Elastron® G P.G401.A90.N | Elastron USA, Inc. | SEBS | Elastron® G |
| Karina IVORY PVC COMPOUND -E 70900-35/ 1-E-AC | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| PENTAMID AHT GV30 H1 schwarz | PENTAC Polymer GmbH | Nylon 46 | PENTAMID AHT |