Calsak ABS CS-72L
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Calsak Polymers |
| Trademark: | Calsak ABS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | cZ5mAP_Calsak-ABS-CS-72L.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Calsak ABS CS-72L is an acrylonitrile butadiene styrene (ABS) product,. It can be processed by injection molding and is available in North America. Features include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.04 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 200°C/5.0 kg | 2.0 | g/10 min | ASTM D1238 |
| 230°C/3.8 kg | 7.0 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 107 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1(3.18 mm) | 2080 | MPa | ASTM D638 |
| Tensile Strength 2(Yield, 3.18 mm) | 44.8 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 40 | % | ASTM D638 |
| Flexural Modulus 3(3.18 mm) | 2450 | MPa | ASTM D790 |
| Flexural Strength 4(3.18 mm) | 72.4 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 340 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.18 mm) | 91.1 | °C | ASTM D648 |
| Vicat Softening Temperature | 93.0 | °C | ASTM D1525 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.59 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 - 87.8 | °C | |
| Drying Time | 2.0 | hr | |
| Rear Temperature | 235 - 249 | °C | |
| Middle Temperature | 241 - 254 | °C | |
| Front Temperature | 246 - 260 | °C | |
| Nozzle Temperature | 246 - 260 | °C | |
| Processing (Melt) Temp | 246 - 302 | °C | |
| Mold Temperature | 43.3 - 65.6 | °C | |
| Injection Pressure | 68.9 - 110 | MPa | |
| Injection Rate | Fast | ||
| Back Pressure | 0.00 - 0.172 | MPa | |
| Clamp Tonnage | 2.8 - 5.5 | kN/cm² |
| Injection instructions |
|---|
| Hold Pressure: 50 to 75% of injection pressureScrew Speed: Moderate |
| Note Message | |
|---|---|
| 1 . | Type 1 |
| 2 . | Type 1 |
| 3 . | Type 1 |
| 4 . | Type 1 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MAZMID B 150 | Mazzaferro Indústria e Comércio de Polímeros e Fibras Ltda. | Nylon 6 | MAZMID B |
| Beetle® PBTS120S | Teknor Apex Company (Chem Polymer) | PBT | Beetle® |
| Geon™ Vinyl Flexible P484B | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Flexible |
| Karina GRAY PVC COMPOUND 828-18/423-AY-ERYB-PO | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Lutene® H BE0400 | LG Chem Ltd. | HDPE | Lutene® H |