Bio-Flex® F 1138
| Category: | PLA , Polylactic Acid |
| Manufacturer: | FKuR Kunststoff GmbH |
| Trademark: | Bio-Flex® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | cYppL1_Bio-Flex-F-1138.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Biodegradable and compostable compound for film extrusion, certified according to EN 13432. Used in applications such as T-shirt bags and waste bags. Bio-Flex® F 1138 / Bio-Flex® Shopper (previously Bio-Flex® V 2878) |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.47 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 2.0 to 4.5 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (190°C/2.16 kg) | 1.50 to 3.50 | cm³/10min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 405 | MPa | ISO 527-2 |
| Tensile Stress | ISO 527-2 | ||
| Yield | 16.0 | MPa | |
| Break | 14.0 | MPa | |
| Tensile Strain (Break) | 370 | % | ISO 527-2 |
| Flexural Modulus | 390 | MPa | ISO 178 |
| Flexural Stress (3.5% Strain) | 10.0 | MPa | ISO 178 |
| Flexural Strain at Break | No Break | ISO 178 | |
| Tensile Strain at Tensile Strength | 360 | % | ISO 527 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tear Propagation Resistance | ISO 6383-2 | ||
| Elmendorf - MD : 20.0 µm | 140 | kN/m | |
| Elmendorf - TD : 20.0 µm | 300 | kN/m | |
| Film Thickness - Tested | 20 | µm | |
| Tensile Modulus | ISO 527-3 | ||
| MD : 20 µm | 530 | MPa | |
| TD : 20 µm | 465 | MPa | |
| Tensile Stress | ISO 527-3 | ||
| MD : Yield, 20 µm | 30.0 | MPa | |
| TD : Yield, 20 µm | 22.0 | MPa | |
| MD : Break, 20 µm | 29.0 | MPa | |
| TD : Break, 20 µm | 21.0 | MPa | |
| Tensile Elongation | ISO 527-3 | ||
| MD : Yield, 20 µm | 280 | % | |
| TD : Yield, 20 µm | 400 | % | |
| MD : Break, 20 µm | 280 | % | |
| TD : Break, 20 µm | 400 | % |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature (DSC) | > 155 | °C | ISO 3146 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 2299 X 120337 | RTP Company | PEEK | RTP |
| SEQUEL® 1780 | LyondellBasell Industries | TPO (POE) | SEQUEL® |
| Vydyne® 21SPF1 | Ascend Performance Materials Operations LLC | Nylon 66 | Vydyne® |
| Boda BDF-KK2801 | Chenguang Fluoro & Silicone Elastomers Co., Ltd. | Fluorelastomer | Boda |
| Karina GRAY PVC COMPOUND 702-DA-18/406-BZ-AS (***) | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |