Order Products : sales@su-jiao.com
OP - PPS 40GF
| Category: | PPS , Polyphenylene Sulfide |
| Manufacturer: | Oxford Polymers |
| Trademark: | OP - PPS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | cYi2lS_OP---PPS-40GF.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| OP - PPS 40GF is a Polyphenylene Sulfide (PPS) material filled with 40% glass fiber. It is available in North America for injection molding. Primary attribute of OP - PPS 40GF: Flame Rated. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.60 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.20 to 0.30 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield | 131 | MPa | |
| Break | 131 | MPa | |
| Flexural Modulus | 11400 | MPa | ASTM D790 |
| Flexural Strength | 165 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (4°C) | 53 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 3.18 mm | 266 | °C | |
| 1.8 MPa, Unannealed, 3.18 mm | 260 | °C |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.59 mm | V-0 | ||
| 3.18 mm | V-0 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 93.3 to 121 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Rear Temperature | 288 to 316 | °C | |
| Middle Temperature | 288 to 307 | °C | |
| Front Temperature | 288 to 307 | °C | |
| Processing (Melt) Temp | 293 to 321 | °C | |
| Mold Temperature | 135 to 177 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 9663-70 Clear | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Ultramid® C33L 01 | BASF Corporation | Nylon 66/6 | Ultramid® |
| BJB Polyurethane ST-3080 A/B | BJB Enterprises, Inc. | TSU | BJB Polyurethane |
| Hipolyene 1533 VW | Zylog Plastalloys | TPO (POE) | Hipolyene |
| LUVOCOM® 65/XCF/30 | Lehmann & Voss & Co. | PP Copolymer | LUVOCOM® |