Tenac™-C CF454
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | Asahi Kasei Chemicals Corporation |
| Trademark: | Tenac™-C |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | cXrdHb_Tenac--C-CF454.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Tenac™-C CF454 is an Acetal (POM) Copolymer product filled with carbon fiber. It is available in Africa & Middle East, Asia Pacific, Europe, or North America. Applications of Tenac™-C CF454 include engineering/industrial parts and housings. Characteristics include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.46 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 4.0 | g/10 min | ISO 1133 |
| Molding Shrinkage | Internal Method | ||
| Flow | 0.10 to 0.20 | % | |
| Across Flow | 0.60 to 0.80 | % | |
| Water Absorption (23°C, 24 hr, 50% RH) | 0.20 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 104 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 13000 | MPa | ISO 527-2 |
| Tensile Stress | |||
| Break | 130 | MPa | ISO 527-2 |
| -- | 118 | MPa | ASTM D638 |
| Tensile Elongation | |||
| Break | 5.0 | % | ASTM D638 |
| Break | 1.0 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 12200 | MPa | ASTM D790 |
| -- | 12500 | MPa | ISO 178 |
| Flexural Strength | 185 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 5.0 | kJ/m² | ISO 179 |
| Notched Izod Impact | 39 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed | 166 | °C | ASTM D648, ISO 75-2/B |
| 1.8 MPa, Unannealed | 163 | °C | ASTM D648, ISO 75-2/A |
| CLTE | |||
| Flow | 4.0E-5 | cm/cm/°C | ASTM D696 |
| Flow | 4.0E-5 to 9.0E-5 | cm/cm/°C | ISO 11359-2 |
| Transverse | 9.0E-5 | cm/cm/°C | ASTM D696 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (0.750 mm) | HB | UL 94 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ultramid® A3ZG7 HP BK20465 | BASF Corporation | Nylon 66 | Ultramid® |
| ACCUTECH™ CP0437M10L | ACLO Compounders Inc. | PP Copolymer | ACCUTECH™ |
| Cheng Yu FV30G25 | Cheng Yu Plastic Company Limited | Acetal (POM) Homopolymer | Cheng Yu |
| Hanwha Total PP FB71 | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | PP, Unspecified | Hanwha Total PP |
| Karina GRAY PVC COMPOUND 802D18/441-CY-IS-AS-BZ | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |