Infino AE-2150
| Category: | PC+PET , Polycarbonate + PET |
| Manufacturer: | LOTTE ADVANCED MATERIALS CO., LTD. |
| Trademark: | Infino |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | cXS6DF_InfinoAE2150.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Infino AE-2150 is a polycarbonate PET (PC PET) product,. It is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific. Typical application areas are: automotive industry. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity (Natural) | 1.33 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (260°C/5.0 kg) | 34 | g/10 min | ASTM D1238, ISO 1133 |
| Molding Shrinkage | |||
| Flow : 3.20mm | 0.40 - 0.60 | % | ASTM D955 |
| Transverse flow : 3.20mm | 0.50 - 0.70 | % | ASTM D955 |
| Lateral flow : 3.20mm | 0.50 - 0.70 | % | ISO 2577 |
| Traffic : 3.20mm | 0.40 - 0.60 | % | ISO 2577 |
| Ash Content | |||
| -- | 15 | % | ASTM D5630 |
| -- | 15 | % | ISO 3451 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | |||
| Class r | 110 | ASTM D785 | |
| R scale | 110 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 3500 | MPa | ASTM D638 |
| -- | 3800 | MPa | ISO 527-2/5 |
| Tensile Strength | |||
| Yield 2 | 66.0 | MPa | ASTM D638 |
| Yield | 63.0 | MPa | ISO 527-2/5 |
| Fracture 3 | 59.0 | MPa | ASTM D638 |
| Fracture | 58.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Fracture 4 | 7.0 | % | ASTM D638 |
| Fracture | 4.0 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| -- 5 | 3900 | MPa | ASTM D790 |
| -- 6 | 4000 | MPa | ISO 178 |
| Flexural Strength | |||
| -- 7 | 86.0 | MPa | ASTM D790 |
| -- 8 | 100 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 9(23°C) | 6.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength 10(23°C) | 85 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact | |||
| -30°C, 3.18 mm | 49 | J/m | ASTM D256 |
| -30°C, 6.35 mm | 49 | J/m | ASTM D256 |
| 23°C, 3.18 mm | 59 | J/m | ASTM D256 |
| 23°C, 6.35 mm | 59 | J/m | ASTM D256 |
| -30°C 11 | 6.0 | kJ/m² | ISO 180/1A |
| 23°C 12 | 7.0 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, unannealed, 6.40mm | 130 | °C | ASTM D648 |
| 0.45 MPa, unannealed, 4.00mm | 129 | °C | ISO 75-2/B |
| 1.8 MPa, unannealed, 6.40mm | 123 | °C | ASTM D648 |
| 1.8 MPa, not annealed, 4.00mm | 112 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 140 | °C | ISO 306/B50 |
| Linear thermal expansion coefficient | ASTM E831, ISO 11359-2 | ||
| Flow : -40 to 40°C | 4.6E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Lateral : -40 to 40°C | 6.6E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| -- | 110 | °C | |
| Hot air dryer | 110 | °C | |
| Drying Time | |||
| -- | 4.0 - 6.0 | hr | |
| Hot air dryer | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 240 - 250 | °C | |
| Middle Temperature | 240 - 260 | °C | |
| Front Temperature | 250 - 270 | °C | |
| Nozzle Temperature | 250 - 270 | °C | |
| Mold Temperature | 60 - 80 | °C | |
| Injection Pressure | 58.8 | MPa | |
| Back Pressure | 0.490 - 1.96 | MPa | |
| Screw Speed | 50 - 100 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 5.0 mm/min |
| 3 . | 5.0 mm/min |
| 4 . | 5.0 mm/min |
| 5 . | 2.8 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 2.8 mm/min |
| 8 . | 2.0 mm/min |
| 9 . | Thickness: 4mm |
| 10 . | Thickness: 4mm |
| 11 . | Thickness: 4mm |
| 12 . | Thickness: 4mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 1383 P-1 | RTP Company | PPS | RTP |
| S&E General Purpose G-4285UV | S&E Specialty Polymers, LLC | PVC, Unspecified | S&E General Purpose |
| Sicoklar E01.28 | Ravago Group | PC | Sicoklar |
| Next Nylon 66 Prime Series PMS1-01S.GY | Next Polymers Ltd. | Nylon 66 | Next Nylon 66 Prime Series |
| Karina IVORY PVC COMPOUND 105850-35/ 1-B-ISE-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |