Salflex 610TIM
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | Salflex Polymers Ltd. |
| Trademark: | Salflex |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | cWSGci_Salflex-610TIM.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Salflex 610TIM is a polypropylene copolymer (PP Copoly) product, which contains 10% talc filler. It can be processed by injection molding and is available in North America. The application fields of Salflex 610TIM include automobile industry, electrical appliances and industrial applications. Features include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.980 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 19 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 1.1 - 1.3 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 92 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Modulus | 1990 | MPa | ASTM D790 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 29.0 | MPa | ASTM D412 |
| Tensile Elongation (Break) | 48 | % | ASTM D412 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 69 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 126 | °C | ASTM D648 |
| Additional Information |
|---|
| Ash Content, ASTM D2584: 12% |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 - 90.0 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Rear Temperature | 190 - 215 | °C | |
| Middle Temperature | 200 - 235 | °C | |
| Front Temperature | 210 - 245 | °C | |
| Nozzle Temperature | 215 - 245 | °C | |
| Processing (Melt) Temp | 200 - 220 | °C | |
| Mold Temperature | 27.0 - 60.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Celstran® PP-GF30-0405 P10/10 | Celanese Corporation | PP, Unspecified | Celstran® |
| Hostacom BG722AC | LyondellBasell Industries | PP Copolymer | Hostacom |
| Jam HDPE HM9455F1 | Jam Petrochemical Company | HDPE | Jam HDPE |
| Karina WHITE PVC COMP E 856-10/189-IS-SD | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Durethan® AKV 30 XTS1 901510 | LANXESS GmbH | Nylon 66 | Durethan® |