LEXAN™ GF1311R resin
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics Asia Pacific |
| Trademark: | LEXAN™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | cWO9Kt_LEXAN-GF1311R-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Lexan* GF1311R Polycarbonate (PC) resin is a 15% glass fiber filled, injection moldable grade. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.29 | g/cm³ | ASTM D792 |
| Melt Volume-Flow Rate (MVR) (300°C/1.2 kg) | 5.00 | cm³/10min | ASTM D1238 |
| Molding Shrinkage | Internal Method | ||
| Flow : 3.20 mm | 0.20 to 0.50 | % | |
| Across Flow : 3.20 mm | 0.20 to 0.50 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 4170 | MPa | ASTM D638 |
| Tensile Strength 2 | ASTM D638 | ||
| Yield | 73.0 | MPa | |
| Break | 60.0 | MPa | |
| Tensile Elongation 3 | ASTM D638 | ||
| Yield | 3.7 | % | |
| Break | 5.9 | % | |
| Flexural Modulus 4(50.0 mm Span) | 3960 | MPa | ASTM D790 |
| Flexural Strength 5 | ASTM D790 | ||
| Yield, 50.0 mm Span | 129 | MPa | |
| Break, 50.0 mm Span | 127 | MPa |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 95 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.20 mm) | 138 | °C | ASTM D648 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Hopper Temperature | 60.0 to 80.0 | °C | |
| Rear Temperature | 270 to 300 | °C | |
| Middle Temperature | 280 to 310 | °C | |
| Front Temperature | 290 to 320 | °C | |
| Nozzle Temperature | 280 to 310 | °C | |
| Processing (Melt) Temp | 290 to 320 | °C | |
| Mold Temperature | 80.0 to 120 | °C |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Mirakutoran® TPU E595PUOO | Japan Mirakutoran Inc. | TPU Alloy | Mirakutoran® TPU |
| SILVER® EUL60-K/SVJ/SJT-45P | Guangdong Silver Age Sci & Tech. Co., Ltd | PVC, Unspecified | SILVER® |
| SUNFROST® KF65GA | Mitsubishi Chemical Performance Polymers, Inc. | PVC Elastomer | SUNFROST® |
| KOCETAL® K300BBK | Kolon Plastics, Inc. | Acetal (POM) Copolymer | KOCETAL® |
| Huafon JF-W-AL3065 | Huafon Group Co., Ltd. | PUR, Unspecified | Huafon |