Boltaron 9200
| Category: | PMMA+PVC , Acrylic (PMMA) + PVC |
| Manufacturer: | Boltaron Performance Products |
| Trademark: | Boltaron |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | cVmr02_Boltaron-9200.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Boltaron 9200 is a proprietary, extruded thermoplastic sheet, designed for use as aircraft window shades. Boltaron 9200 offers maximum light blocking characteristics, excellent impact strength, abrasion resistance, stain and chemical resistance, and thermoformability. Boltaron 9200 meets stringent FAA regulations for flammability, smoke generation and heat release as set forth in FAR 25.853 paragraphs (a) and (d). Boltaron 9200 is available as a single color (9200) or as a double color (9200C) construction. Colors: Custom Gauges: .047 to .060 Widths: Up to 48" Lengths: Up to 120" Textures: Coarse Matte (CM) Felt (FT) Haircell (HC) Levant (LT) Mesa (MS) Suede (SD) |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.49 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.50 to 0.70 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 112 to 115 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 40.0 to 44.1 | MPa | ASTM D638 |
| Flexural Modulus | 3030 to 3170 | MPa | ASTM D790 |
| Flexural Strength (Yield) | 68.9 to 72.4 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 53 to 110 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Annealed) | 75.6 to 77.8 | °C | ASTM D648 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flammability | FAR 25.853 | ||
| 12 sec | Pass | ||
| 60 sec | Pass | ||
| Heat Release | FAR 25.853 | ||
| 2 min | < 65 | kW·min/m² | |
| Peak | < 65 | kW/m² |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ds | ASTM F814 | ||
| 1.5 min | < 100 | ||
| 4 min | < 200 | ||
| Forming Temperature | 168 to 185 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Taitacell EPS 301MM | Taita Chemical Company, Ltd. | PS (EPS) | Taitacell |
| NORYL™ APS430 resin | SABIC Innovative Plastics Asia Pacific | PPS+PPE | NORYL™ |
| Ferro PP TPP40AC28HB-NA | Ferro Corporation | PP Homopolymer | Ferro PP |
| Dynaprene® SE9040A | Nantex Industry Co., Ltd. | TPE | Dynaprene® |
| LNP™ LUBRILOY™ Lexan_WR6300 compound | SABIC Innovative Plastics | AES+PC+SAN | LNP™ LUBRILOY™ |