Badamid® PA612 GF50
| Category: | Nylon 612 , Polyamide 612 |
| Manufacturer: | Bada AG |
| Trademark: | Badamid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | cVFLfR_Badamid-PA612-GF50.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Badamid® PA612 GF50 is a Polyamide 612 (Nylon 612) material filled with 50% glass fiber. It is available in Europe for injection molding. Primary attribute of Badamid® PA612 GF50: Flame Rated. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.51 | -- | g/cm³ | ISO 1183 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus 1(23°C) | 13800 | 11900 | MPa | ISO 527-2/1 |
| Tensile Stress 2(Break, 23°C) | 195 | 178 | MPa | ISO 527-2/1A/5 |
| Tensile Strain 3(Break, 23°C) | 2.5 | 2.9 | % | ISO 527-2/5 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 20 | -- | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 90 | -- | kJ/m² | ISO 179/1eU |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 212 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 205 | -- | °C | ISO 75-2/A |
| Melting Temperature (DSC) 4 | 218 | -- | °C | ISO 3146 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Volume Resistivity (1.00 mm) | 1.0E+12 | -- | ohms·cm | IEC 60093 |
| Electric Strength (1.00 mm) | 35 | -- | kV/mm | IEC 60243-1 |
| Comparative Tracking Index | 550 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 0.800 mm | HB | -- | ||
| 1.60 mm | HB | -- |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Processing (Melt) Temp | 240 to 280 | °C | |
| Mold Temperature | 60.0 to 90.0 | °C |
| Note Message | |
|---|---|
| 1 . | Test Specimen accordng to ISO 3167, Type A |
| 2 . | Test Specimen accordng to ISO 3167, Type A |
| 3 . | Test Specimen accordng to ISO 3167, Type A |
| 4 . | 10 K/Min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Makrolon® 2865 | Covestro - Polycarbonates | PC | Makrolon® |
| Versaflex™ HC MT226 | PolyOne Corporation | TPE | Versaflex™ |
| Hostacom Premium TBC 141N | LyondellBasell Industries | Polyolefin, Unspecified | Hostacom |
| Karina BLUE PVC COMP. -E550D06/957 | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Lucon® CP2100 | LG Chem Ltd. | PC | Lucon® |