LG PMMA HI535
| Category: | Acrylic (PMMA) , Polymethyl Methacrylate Acrylic |
| Manufacturer: | LG MMA Corp. |
| Trademark: | LG PMMA |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | cUvNQW_LG-PMMA-HI535.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LG PMMA HI535 is a Polymethyl Methacrylate Acrylic material. It is available in Asia Pacific, Europe, Latin America, or North America. Important attributes of LG PMMA HI535 are:
|
| General Information | |
|---|---|
| Features |
|
| RoHS Compliance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.17 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/3.8 kg) | 1.8 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.40 to 0.80 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.40 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 57 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 43.1 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | 120 | % | ASTM D638 |
| Flexural Modulus | 1830 | MPa | ASTM D790 |
| Flexural Strength (Yield) | 76.5 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 5.5 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | 60 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact (Area) | 5.60 | kJ/m² | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 85.0 | °C | ASTM D648 |
| Vicat Softening Temperature | 99.0 | °C | ASTM D1525 1 |
| CLTE - Flow | 7.0E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | > 1.0E+15 | ohms·cm | ASTM D257 |
| Dielectric Strength 2 | 15 | kV/mm | ASTM D149 |
| Dielectric Constant (60 Hz) | 3.10 | ASTM D150 | |
| Dissipation Factor (60 Hz) | 0.040 | ASTM D150 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Refractive Index | 1.490 | ASTM D542 | |
| Transmittance (3200 µm) | 90.0 | % | ASTM D1003 |
| Haze (3200 µm) | < 1.5 | % | ASTM D1003 |
| Note Message | |
|---|---|
| 1 . | Loading 1 (10 N) |
| 2 . | 4000 V/sec |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP ESD C 2800 B-75A | RTP Company | TPO (POE) | RTP |
| Texalan® 5 Series 582A | Austin Novel Materials Co. Ltd. | TPU-Polyester | Texalan® 5 Series |
| LNP™ THERMOCOMP™ PX87791 compound | SABIC Innovative Plastics | Nylon 6 | LNP™ THERMOCOMP™ |
| Lupoy® 3030-15 | LG Chem Ltd. | PC | Lupoy® |
| Sylvin 8200-85 White 1515 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |