3M™ Dyneon™ Fluoroelastomer FE 5840Q

Category:	Fluorelastomer , Fluoroelastomer
Manufacturer:	3M Advanced Materials Division
Trademark:	3M™ Dyneon™ Fluoroelastomer
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	cSEDEo_3MDyneonFluoroelastomerFE5840Q.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

Message
3M™ Dyneon™ Fluoroelastomer FE 5840Q is a terpolymer made from hexafluoropropylene, vinylidene fluoride and tetrafluoroethylene. FE 5840Q has an incorporated bisphenol cure system. Special Features Composition: Terpolymer of vinylidene fluoride, hexafluoropropylene and tetrafluoroethylene Process targets: compression, injection and transfer moulding Recommended alternative for 3M™ Dyneon™ Fluoroelastomer FX 9038 Recommended for automotive fuel system applications Excellent mould release Proprietary incorporated cure technology Clean running Typical Applications 3M™ Dyneon™ Fluoroelastomer FE 5840Q is a high fluorine material designed for O-ring and gasket applications.

Message

3M™ Dyneon™ Fluoroelastomer FE 5840Q is a terpolymer made from hexafluoropropylene, vinylidene fluoride and tetrafluoroethylene. FE 5840Q has an incorporated bisphenol cure system.

Special Features

Composition: Terpolymer of vinylidene fluoride, hexafluoropropylene and tetrafluoroethylene

Process targets: compression, injection and transfer moulding

Recommended alternative for 3M™ Dyneon™ Fluoroelastomer FX 9038

Recommended for automotive fuel system applications

Excellent mould release

Proprietary incorporated cure technology

Clean running

Typical Applications
3M™ Dyneon™ Fluoroelastomer FE 5840Q is a high fluorine material designed for O-ring and gasket applications.

General Information
Features	Terpolymer Good demoulding performance
Uses	O-rings Washer
Appearance	Opacity White-like
Forms	Thick sheet
Processing Method	Resin transfer molding Compression molding Injection molding

Physical	Nominal Value	Unit	Test Method
Specific Gravity	1.89	g/cm³	Internal method
Mooney Viscosity (ML 1+10, 121°C)	37	MU	Internal method
Fluorine Content	70	%	Internal method

Hardness	Nominal Value	Unit	Test Method
Durometer Hardness (Shore A)	86		ASTM D2240

Elastomers	Nominal Value	Unit	Test Method
Tensile Stress ¹(100% Strain)	6.00	MPa	ASTM D412A
Tensile Strength ²	15.0	MPa	ASTM D412A
Tensile Elongation ³(Break)	240	%	ASTM D412A
Compression Set			ASTM D1414
200°C, 70 hr ⁴	35	%	ASTM D1414
200°C, 70 hr ⁵	43	%	ASTM D1414

Note Message
1 .	D mould
2 .	Die D
3 .	D mould
4 .	Post cured 16 hours @ 230°C
5 .	Post cured 24 hours @ 260°C

Resin Grade	Manufacturer	Category	Trademark
TECHNO ABS TFX-SBT3	Techno Polymer Co, Ltd.	ABS	TECHNO ABS
ElectriPlast® EP-SS/PP	Integral Technologies, Inc.	PP, Unspecified	ElectriPlast®
LNP™ THERMOCOMP™ WX05505 compound	SABIC Innovative Plastics	PBT	LNP™ THERMOCOMP™
Plaslube® NY-1/SI/5	Techmer Engineered Solutions	Nylon 66	Plaslube®
Sylvin 8474-80 Black	Sylvin Technologies Incorporated	PVC+NBR	Sylvin