Kingfa PET-RG30
| Category: | PET , Polyethylene Terephthalate |
| Manufacturer: | Kingfa |
| Trademark: | Kingfa |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | cN3BdW_Kingfa-PET-RG30.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Kingfa PET-RG30 is a polyethylene terephthalate (PET) material, which contains a 30% glass fiber reinforced material. This product is available in North America or Asia Pacific region. The processing method is injection molding. The main features of Kingfa PET-RG30 are:
The typical application areas of Kingfa PET-RG30 are: electrical/electronic applications |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.65 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 23°C | 0.30 | % | ASTM D955 |
| Transverse flow : 23°C | 0.90 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.070 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 120 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | 140 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 2.3 | % | ASTM D638 |
| Flexural Modulus 3 | 10500 | MPa | ASTM D790 |
| Flexural Strength 4 | 210 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.20 mm) | 80 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, unannealed, 6.40mm | 240 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 6.40mm | 225 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+16 | ohms·cm | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.750 mm | V-0 | UL 94 | |
| 3.00 mm | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 - 140 | °C | |
| Drying Time | 3.0 - 5.0 | hr | |
| Rear Temperature | 235 - 255 | °C | |
| Middle Temperature | 245 - 265 | °C | |
| Front Temperature | 255 - 275 | °C | |
| Processing (Melt) Temp | 255 - 275 | °C | |
| Mold Temperature | 80.0 - 120 | °C | |
| Injection Rate | Moderate-Fast |
| Injection instructions |
|---|
| Processing Temperature Limit: 270°C |
| Note Message | |
|---|---|
| 1 . | 10 mm/min |
| 2 . | 10 mm/min |
| 3 . | 2.0 mm/min |
| 4 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ravathane R210D52UV | RAVAGO Kimya Plastik Sanayi ve Ticaret A.S. | TPU-Polyether | Ravathane |
| Vydyne® 41H NT | Ascend Performance Materials Operations LLC | Nylon 66 | Vydyne® |
| FARALLOY® PP-205 | O'Neil Color and Compounding | PP, Unspecified | FARALLOY® |
| Karina STRAW PVC COMPOUND 751-38/117-B-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| TECACOMP® PA66 TC white 3924 | Ensinger GmbH | Nylon 66 | TECACOMP® |