CERTENE™ LLBF-120F
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | Muehlstein |
| Trademark: | CERTENE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | cMXQkM_CERTENE-LLBF-120F.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| LLBF-120F is a certified prime resin with Butene-comonomer, designed for production of Blown films used in general purpose packaging. LLBF-120F features excellent combination of easy processability with good film strength as well as wide heat sealing temperature range. LLBF-120F applications include garment bags, produce bags and liners. LLBF-120F contains high slip and high antiblock. LLBF-120F complies with FDA regulation 21CFR 177.1520(c)3.1a and with most international regulations concerning the use of Polyethylene in contact with food articles. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.920 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.0 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 25 | µm | |
| secant modulus | ASTM D882 | ||
| 1% secant, MD : 25 µm | 193 | MPa | ASTM D882 |
| 1% secant, TD : 25 µm | 223 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 25 µm | 9.38 | MPa | ASTM D882 |
| TD : Yield, 25 µm | 9.51 | MPa | ASTM D882 |
| MD : Break, 25 µm | 34.5 | MPa | ASTM D882 |
| TD : Break, 25 µm | 27.6 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 25 µm | 550 | % | ASTM D882 |
| TD : Break, 25 µm | 820 | % | ASTM D882 |
| Dart Drop Impact 1(25 µm) | 85 | g | ASTM D1709A |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 25 µm | 100 | g | ASTM D1922 |
| TD : 25 µm | 600 | g | ASTM D1922 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 25.4 µm, Blown Film) | 35 | ASTM D2457 | |
| Haze (25.4 µm, Blown Film) | 20 | % | ASTM D1003 |
| Additional Information |
|---|
| Film Specimen: 1.0 mils (25 µm) film using barefoot version; melt temperature 390-395°F; blow-up-ratio 2.5 :1. |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 199 - 202 | °C |
| Note Message | |
|---|---|
| 1 . | F50 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYMAN® (ABS) LP 299/2 GL A | A. Schulman Europe | ABS | POLYMAN® |
| SCLAIR® 14G | NOVA Chemicals | MDPE | SCLAIR® |
| Tarnamid® T-27 GF25 MT15 | Grupa Azoty S.A. | Nylon 6 | Tarnamid® |
| UNIBRITE® UB-801 | Nippon A&L Inc. | AES | UNIBRITE® |
| Durethan® DP 2325 H3.0 000000 | LANXESS Asia/Pacific | Nylon 66 | Durethan® |