FORMULA P ELAN 5220 M2 Z
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Putsch Kunststoffe GmbH |
| Trademark: | FORMULA P |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | cMTfuQ_FORMULA-P-ELAN-5220-M2-Z.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polypropylene, with 20% mineral reinforcement. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.04 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 12 | g/10 min | ISO 1133 |
| Molding Shrinkage | 0.80 - 1.0 | % | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2 | ||
| Yield | 21.0 | MPa | ISO 527-2 |
| Fracture | 14.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 50 | % | ISO 527-2 |
| Flexural Modulus | 2000 | MPa | ISO 178 |
| Flexural Stress (3.5% Strain) | 37.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ISO 180 | ||
| -20°C | 4.0 | kJ/m² | ISO 180 |
| 23°C | 18 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 64.0 | °C | ISO 306/B |
| Additional Information |
|---|
| Tensile Strength, ISO 527: 21 MPa |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 | hr | |
| Processing (Melt) Temp | 250 - 270 | °C | |
| Mold Temperature | 30.0 - 60.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 2399C X 68917 A | RTP Company | TPU, Unspecified | RTP |
| Desmopan® DP 85786A | Covestro - PUR | TPU, Unspecified | Desmopan® |
| DELPET™ SRB235 | Asahi Kasei Chemicals Corporation | Acrylic (PMMA) | DELPET™ |
| Karina IVORY PVC COMPOUND TR-781-35/1-B-IS (*) | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Ultramid® HFX 32 BK00464 | BASF Corporation | Nylon 6 | Ultramid® |